Properties of fibers based on polyhydroxybutyrate
Štulrajterová, Lujza ; Tocháček, Jiří (oponent) ; Přikryl, Radek (vedoucí práce)
This work deals with the melt spinning process of biopolymer fibers. Recent knowledge of poly(3-hydroxy butyrate) (PHB) and poly(lactic acid) (PLA) fiber spinning processes have been covered in the theoretical part. PHB based polymer blends of various composition were prepared to study the effect of PLA, different plasticizers and their content on the fiber properties. Three commercial plasticizers (ATBC, PEG, A6) and two experimentally synthesized were used. Spinning was carried out on three devices. Spinning on the conventional spinning lines with take-up speed exceeding 150 m/min was not accomplished. Lowe take-up speed was necessary due to insufficient melt strength. Fibers with drawing ratio of 6.4 were prepared and analyzed by GPC, MDSC and mechanical testing. According to the glass transition temperature results, ATBC and PEG have better plasticizing effect over the studied PLA/PHB blends than A6. Fibers containing A6 have the highest tensile strength and modulus of elasticity of 250 MPa and 2.7 GPa, respectively. At last, the effect of aging, thermal and hydrothermal treatment on mechanical properties of fibers was studied.
|
|
|
Biodegradabilní termoplastické materiály z obnovitelných surovin
Březinová, Štěpánka ; Kučera, František (oponent) ; Petruš, Josef (vedoucí práce)
Předložená diplomová práce v teoretické části shrnuje dosavadní poznatky v oblasti biodegradabilních termoplastických materiálů s důrazem na polymerní materiály z obnovitelných zdrojů a možnosti jejich zpracování a modifikace užitných vlastností. Experimentální část práce je zaměřena na přípravu a charakterizaci biodegradabilních polymerních směsí na bázi termoplastického škrobu (TPS) a poly(butylenadipát-co-tereftalátu) (ECX). Vhodný typ TPS byl vybrán na základě reologického chování taveniny pro mísení s ECX technologií extruze. Míra kompatibility TPS a ECX byla zhodnocena pomocí infračervené spektroskopie (FTIR-ATR) a pozorováním morfologie TPS/ECX směsí skenovací elektronovou mikroskopií (SEM). Možnost ovlivnění mechanických vlastností, reologického chování a navlhavosti připravených TPS/ECX byla ověřena testováním mechanických vlastností při namáhání v tahu, stanovením indexu toku taveniny (MFI), oscilačním reologickým testem a stanovením maximální navlhavosti. Z experimentálně získaných výsledků vyplývá možnost optimalizace mechanických a reologických vlastností TPS mísením s ECX, zatímco z pohledu biodegradability lze přepokládat za výhodnější směsi s majoritním obsahem TPS.
|
|
|
Properties of fibers based on polyhydroxybutyrate
Štulrajterová, Lujza ; Tocháček, Jiří (oponent) ; Přikryl, Radek (vedoucí práce)
This work deals with the melt spinning process of biopolymer fibers. Recent knowledge of poly(3-hydroxy butyrate) (PHB) and poly(lactic acid) (PLA) fiber spinning processes have been covered in the theoretical part. PHB based polymer blends of various composition were prepared to study the effect of PLA, different plasticizers and their content on the fiber properties. Three commercial plasticizers (ATBC, PEG, A6) and two experimentally synthesized were used. Spinning was carried out on three devices. Spinning on the conventional spinning lines with take-up speed exceeding 150 m/min was not accomplished. Lowe take-up speed was necessary due to insufficient melt strength. Fibers with drawing ratio of 6.4 were prepared and analyzed by GPC, MDSC and mechanical testing. According to the glass transition temperature results, ATBC and PEG have better plasticizing effect over the studied PLA/PHB blends than A6. Fibers containing A6 have the highest tensile strength and modulus of elasticity of 250 MPa and 2.7 GPa, respectively. At last, the effect of aging, thermal and hydrothermal treatment on mechanical properties of fibers was studied.
|
|
| |
|
| |
|
|
Výpočty fázových rovnováh pro směsi polymerů
Živný, Antonín
Analyzují se metody výpočtů fázových rovnovah ve směsích polymerů se specifickými interakcemi na bázi kvazichemické Barkerovy teorie. Provádí se zejména numerické řešení rovnice spinodály a následná konstrukce křivek fázové koexistence v těchto systémech.
|
|
| |
|
| |
|
|
Vývoj fázové struktury při toku polymerních směsí
Fortelný, Ivan
Stav popisu vývoje fázové struktury při toku polymerních směsí je diskutován. Je ukázáno, že neexistuje pravidlo pro uspokojivou předpověď typu fázové struktury. Grafické řešení rovnice popisující dynamickou rovnováhu mezi rozpadem a koalescencí kapek poskytuje uspokojivou kvalitativní předpověď závislosti střední velikosti kapky na parametrech systému.
|