Mechanical properties of plasma sprayed layers of NiAl10 and NiAl40 on AZ91 alloy
Kubatík, Tomáš František ; Brodil, R. ; Ctibor, Pavel ; Průša, F. ; Brožek, Vlastimil
In this work, plasma coatings of NiAl10 and NiAl40 on magnesium alloy AZ91 substrate were prepared by the hybrid plasma spraying system WSP®-H 500. The both plasma sprayed coatings of NiAl10 and NiAl40 have metallurgical bond. The thicknesses of microstructures in the cross-section of NiAl10 and NiAl40 plasma sprayed coatings prepared by 9 passes were 374 and 440 μm respectively. Adhesion test of plasma sprayed layers was performed using a modified ASTM C 633 standard. The tensile adhesion strength values are 24.7 MPa for NiAl10 coatings and 12.3 MPa for NiAl40 coatings. Abrasion resistance according to Slurry Abrasion Response (SAR) test of NiAl40 layers had similar values (0.12 g/cm2)in a comparison with the uncoated AZ91 (0.126 g/cm2). Layers NiAl10 had greater weight losses (0.175 g/cm2) than uncoated AZ91. Microhardness of plasma coating of NiAl40 is several times greater than microhardnesses of plasma coating of NiAl10 and uncoated substrate AZ91
|
|
|
Corrosion behavior of plasma coatings CuAl10 and CuAl50 on magnesium alloy AZ 91
Kubatík, Tomáš František ; Stoulil, J. ; Stehlíková, K. ; Slepička, P. ; Janata, Marek
The most common magnesium alloy AZ 91 is widely used as a structural material, but its use is limited at higher temperatures and high humidity. Plasma spraying is a technology that allows to prepare protective metallic and non-metallic coatings on a wide variety of substrates including magnesium and its alloys. In this study, CuAl10 and CuAl50 were plasma sprayed on magnesium alloy AZ 91 with the aim to study corrosion resistance of the plasma sprayed coatings. The corrosion resistance of layers was evaluated by the method of electrochemical potentiodynamic measurement as well as long-term corrosion tests in a condensation chamber with 0.5 mol\nNaCl at the temperature of 35 °C for 1344 hours. Layers with 1, 2, 5 passes and passes of CuAl10 with the thickness ranging from 75 to 716 mm and CuAl50 with the thickness ranging from 64 to 566 mm were prepared. The increased corrosion velocity was observed in the case of thin layers of 2 and 5 passes due to the development of a galvanic corrosion couple. The CuAl10 layer prepared with ten passes has an outstanding corrosion resistance.
|
|
|
Mechanical and chemical properties of plasma sprayed bronze CuAl10 coating on magnesium and magnesium alloy AZ91
Kubatík, Tomáš František ; Vilémová, Monika ; Mušálek, Radek ; Janata, Marek
The most common magnesium alloy AZ91 is widely used as a structural material, but its use is limited at higher temperatures and high humidity. Plasma spraying is a technology that allows to prepare protective metallic and nonmetallic coatings on a wide variety of substrates including magnesium and its alloys. In this study, CuAl10 was plasma sprayed on magnesium and magnesium alloy AZ91 with the aim to study corrosion resistance of the magnesium substrates. The work focuses on optimization of the plasma spraying process, on chemical composition of the coatings, on interface between the coating and substrate, as well as on adhesive strength of the coatings. The coating were deposited after two passes of the spraying torch resulting in thickness of 150 micro m on magnesium substrate and 110 micro m on AZ91 substrate. Chemical microanalysis showed that deposition of CuAl10 alloy on magnesium results in formation of an intermetallic layer at the interface. The layer provides a
|
host ::
RSS.