Development of Creep Damage in Similar Weld Joints of P92 Steel Pipe
 Král, Petr ; Sklenička, Václav ; Kuchařová, Květa ; Svobodová, M. ; Kvapilová, Marie ; Dvořák, Jiří
The microstructure and creep behaviour of the welded joints of P92 steel pipe were\ninvestigated in order to determine the influence of orbital heat welding technology on the creep\nresistance. Creep specimens were machined from the welded joints. Tensile creep tests of welded\njoints were performed at 873 K using different stresses. The microstructure of tested specimens was\ninvestigated by scanning electron microscope Tescan equipped with an electron-back scatter\ndiffraction. The creep results showed that the creep fracture strain of the welded joints decreases\nwith decreasing value of applied stress. Microstructure investigation showed that fracture behaviour\nof welded joints is influenced by an enhanced cavity formation at grain boundaries in the heataffected\nzone causing lower fracture ductility.
Úplný záznam
Creep damage tolerance factor lambda of selected creep-resistant steels
 Sklenička, Václav ; Kuchařová, Květa ; Dvořák, Jiří ; Kvapilová, Marie ; Král, Petr
The creep damage tolerance factor lambda as an important outcome of the continuum damage mechanics approach has been used to asses the creep fracture mode and the susceptibility of material to localized cracking at strain concentrations. In this work, using sets of our earlier published creep data of three advanced ferritic creep-resistant steels (T23 low alloy steel, P91 and P92 chromium steels) are analysed in terms of the creep damage tolerance factor lambda. It was found that the value of the creep damage factor lambda is not constant and depends on the creep loading conditions. The data analysis is followed by fractographic investigations, which is used to identify the creep fracture mode(s) experimentally.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English