Combined coatings against mechanical wear and corrosion low carbon steel
Brožek, Vlastimil ; Pokorný, P. ; Kolísko, J. ; Vokáč, M. ; Mastný, L. ; Stoulil, J.
In this study, special ceramic coatings were prepared on low carbon steel (1.0060 - EN 10027-2) via the plasma spraying technique using a WSP®-H plasma generator with output of up to 40 kg/h of aluminum oxide. Corundum coatings were deposited directly on the surface of steel plungers equipped with an anti-corrosion interlayer of zinc phosphate. Coating adhesion properties were tested using pin-off tests (modified ISO 4624) and reached a maximum value of 26 MPa. Corrosion resistance was evaluated by measurements of impedance spectra in the 100 kHz - 10 mHz range in a water solution of sodium sulfate. The capacity of electric double-layer varied depending on the porosity and thickness of the coating. Low-porosity coatings of >1.5 mm thickness had RCT 1.29·105 Ω·m2. The abrasive resistance of coatings was measured by rotary/machining test with SiC cutting knives, using a downforce of 50 kg·cm-2. Abrasion losses decreased with the quality of finish - starting at 0.00266 g cm-2 min-1 down to virtually zero losses after polishing the surface below Ra = 0.55 micro m.
|
|
|
Výroba, použití a vlastnosti niklových slitin
Kejha, Richard ; Blažík, Petr (oponent) ; Záděra, Antonín (vedoucí práce)
Práce předkládá literární rešerši s problematikou zaměřenou na průmyslové využívané niklové slitiny, zvláště pak na slitiny žáruvzdorné a žáropevné, V práci jsou ppsány základní tržní značky konstrukčních, žáropevných a žáruvzdorných slitin a jejich vybraní představitelé. Dále jsou uvedeny základní vlastnosti daných materiálů a jejich přibližné porovnání. Základními konstrukčními slitinami jsou monelové slitiny na bázi Ni-Cu, které dosahují velice dobrých mechanických vlastností a výborné korozní odolnosti. Materiály žáruvzdorné a žáropevné jsou většinou na bázi Ni-Cr či Ni-Cr-Fe a jejich mechanické vlastnosti jsou velice rozdílné jak za běžných podmínek, tak i za vysokých provozních teplot, protože bývají využity různé druhy legujících prvků a jejich koncentrací. Tyto slitiny jsou obvykle legovány prvky jako W, Cu, V, Al, Nb, Ti, Ta, Mo, Co, Zr, B.
|
|
|
Physical properties of ultrafine-grained polycrystals of magnesium based alloys
Vrátná, Jitka
Předložená diplomová práce se zabývá studiem mikrostruktury, mechanickými vlastnostmi, strukturou poruch a korozní odolností ultrajemnozrnné hořčíkové slitiny AZ31 připravené dvěma po sobě jdoucími procesy: extruzí a metodou ECAP. Vývoj mikrostruktury byl studován pomocí optické a transmisní elektronové mikroskopie a pomocí difrakce zpětně odražených elektronů (EBSD). Mechanické vlastnosti byly zkoumány měřením mikrotvrdosti a tahovými zkouškami, struktura poruch byla pozorována metodou positronové anihilační spektroskopie (PAS). Z tahových zkoušek bylo zjištěno, že charakteristické napětí σ0.2 slabě roste pouze do dvou průchodů ECAP a s každým dalším průchodem poměrně výrazně klesá. Tento průběh napětí σ0.2 odpovídá naměřeným výsledkům z PAS. Měření EBSD prokázalo, že materiál obsahujebimodální strukturu - skládá se z menšího množství velkých zrn, které jsou obklopené malými zrny. Tato bimodální struktura s rostoucím počtem průchodů postupně mizí. Po 8 průchodech již nejsou pozorována žádná hrubá zrna, struktura je homogenní a průměrná velikost zrn se pohybuje v submikronové oblasti. Podíl vysokoúhlových hranic zrn je přibližně 80%. Nejlepší korozní odolnosti ze všech studovaných vzorků bylo dosaženo u vzorku po osmi průchodech ECAP. Tato relativně vysoká odolnost proti korozi je způsobena hlavně...
|
|
|
Effect of microstructure on mechanisms of plastic deformation in fine-grained magnesium alloys
Minárik, Peter
Táto práca sa zaoberá štúdiom vplyvu zjemnenia zrna na mechanické vlastnosti a koroziodolnosť horčíkových zliatin potenciálnych pre použitie v medicíne - AE21 a AE42. Mechanické vlastnosti sa menili s pretláčaním cez ECAP v súlade s literárnymi zdrojmi. Zmenšením zrna bola získaná zvýšená koroziodolnosť v zliatine AE42. Korózna vrstva, vytvorená na povrchu, bola ďalej študovaná pomocou svetelnej a elektronovej mikroskopie. Taktiež bol študovaný efekt veľkosti zrna na charakter koróznej vrstvy. Zliatina AE42 je perspektívna na ďalšie štúdium v oblasti materiálov potenciálnych pre medicínu. Zliatina AE21 bola vylúčená z ďalších štúdií kvôli vysokej korozivite, dokonca aj po pretlačení cez ECAP.
|
|
|
Corrosion behavior of plasma coatings CuAl10 and CuAl50 on magnesium alloy AZ 91
Kubatík, Tomáš František ; Stoulil, J. ; Stehlíková, K. ; Slepička, P. ; Janata, Marek
The most common magnesium alloy AZ 91 is widely used as a structural material, but its use is limited at higher temperatures and high humidity. Plasma spraying is a technology that allows to prepare protective metallic and non-metallic coatings on a wide variety of substrates including magnesium and its alloys. In this study, CuAl10 and CuAl50 were plasma sprayed on magnesium alloy AZ 91 with the aim to study corrosion resistance of the plasma sprayed coatings. The corrosion resistance of layers was evaluated by the method of electrochemical potentiodynamic measurement as well as long-term corrosion tests in a condensation chamber with 0.5 mol\nNaCl at the temperature of 35 °C for 1344 hours. Layers with 1, 2, 5 passes and passes of CuAl10 with the thickness ranging from 75 to 716 mm and CuAl50 with the thickness ranging from 64 to 566 mm were prepared. The increased corrosion velocity was observed in the case of thin layers of 2 and 5 passes due to the development of a galvanic corrosion couple. The CuAl10 layer prepared with ten passes has an outstanding corrosion resistance.
|
|
|
Galvanické zinkování
Půček, František ; Dvořák, Milan (oponent) ; Žák, Ladislav (vedoucí práce)
Cílem této práce je zpracování rešerše a celkový popis metody galvanického zinkování a technologií při ní používaných. Práce se velkou měrou věnuje korozi jako takové a způsobu jejího vzniku a šíření. Dále se klade velký důraz na fyzikálně-chemické děje probíhající na povrchu zinkované součásti při provádění různých technologických metod spojených s galvanickým zinkováním. Velká část této práce se zaměřuje na výběr vhodné metody galvanického zinkování pro dosažení co nejlepších výsledků za poměrně dobrých ekonomických podmínek. V závěru práce se rozebírá celkový proces a možné defekty způsobené na galvanicky vyloučené vrstvě
|
|
|
Hodnocení elektrochemických charakteristik tvářené hořčíkové slitiny AZ31
Hána, Tomáš ; Tkacz, Jakub (oponent) ; Drábiková, Juliána (vedoucí práce)
Tato práce se zabývá problematikou elektrochemické charakterizace tvářené hořčíkové slitiny AZ31, která byla vystavena koroznímu prostředí 0,1 moldm3 roztoku chloridu sodného. Pro vyhodnocení elektrochemických charakteristik jako jsou korozní rychlost, korozní proudová hustota, korozní potenciál a polarizační odpor byly použity metody elektrochemické impedanční spektroskopie a potenciodynamické zkoušky. V teoretické části jsou shrnuty způsoby výroby hořčíkových slitin, vliv legujících prvků na vlastnosti materiálu a typy koroze, které vedou k degradaci materiálu. V experimentální části jsou popsány použité metody, jejich výsledky a nakonec je uvedena diskuze získaných dat a jejich srovnání.
|
|
| |
|
|
Povrchová úprava kulového čepu
Plášil, Petr ; Kubíček, Jaroslav (oponent) ; Žák, Ladislav (vedoucí práce)
Diplomová práce vypracovaná v rámci magisterského navazujícího studia oboru M2I – K analyzuje možné způsoby povrchové ochrany kulového čepu a tím zvýšení jeho korozní odolnosti. Kulový čep je montovaný do několika druhů podvozkových komponentů, např. kloubů, ramen apod. Současný stav je pro výrobce nevyhovující, nedostačující korozní ochrana zvyšuje počet reklamací a to se může odrazit na množství budoucích zakázek. Vhodnou povrchovou úpravou se má docílit vyšší korozní odolnosti při zachování funkčních vlastností používaných čepů.
|
|
|
Korozní a chemická odolnost konverzních povlaků
Palková, Michaela ; Ing. Eva Novotná, Ph.D., Paed IGIP (oponent) ; Tulka, Jaromír (vedoucí práce)
Tato diplomová práce byla zaměřená na studium chemické a korozní odolnosti vybraných konverzních povlaků. V teoretické části byl proveden rozbor problematiky koroze a možností protikorozních ochran se zaměřením na konverzní povlaky zhotovené na povrchu oceli a hliníku. V experimentální části bylo provedeno testování jejich korozní a chemické odolnosti a to jednak bez další povrchové úpravy, a jednak v kombinaci s povlakem zhotoveným pomocí syntetické nátěrové hmoty a práškové nátěrové hmoty na bázi polyesteru.
|