Dispersed reinforcement influence on the maturation of polymercement materials
Zaťko, Petr ; Jakubík, Aleš (referee) ; Bydžovský, Jiří (advisor)
The diploma thesis is focused on polymercement materials with dispersed reinforcement. The aim of this work is development of suitable polymercement mixture and monitoring of the impact of dispersed reinforcement on the course of maturation of these materials and physico-mechanical properties. The effect of high temperatures on the properties of the mortar is also examined. Emphasis is placed on the use of alternative resources and byproducts. Mixed binder of cement and slag and admixture of microsilica was used. Recycled cellulose was used as dispersed reinforcement and was compared with commercial polypropylene fibers.
|
|
|
Comparison of dynamic modulus of elasticity repair materials exposed to thermal stress
Munduchová, Markéta ; Jakubík, Aleš (referee) ; Brožovský, Jiří (advisor)
Diploma thesis is composed of theoretical and practical part. In theoretical part there are findings related to structure changes of concrete exposed to high temperatures. Models used to simulate high temperature exposure of concrete are described in this thesis. Evaluation of internal structure damage is appropriate by using non-destructive methods, which determine dynamic modulus of elasticity in compression and tension. These methods includes ultrasonic impulse method and resonation method and therefore research was made of articles contains these methods. In experimental part of diploma thesis the test specimens was made from repair materials from UTHD and commercially produced repair materials. The test specimens were subjected to thermal load: 200, 400, 600, 800 °C. Damage of internal structure was examined by ultrasonic impulse method and resonation method.
|
|
|
RESEARCH AND DEVELOPMENT COMPOSITE MATERIAL WITH A HIGHER RESISTANCE TO HIGH TEMPERATURES
Válek, Jaroslav ; Durica,, Tibor (referee) ; Kolář,, Karel (referee) ; Sitek,, Libor (referee) ; Bodnárová, Lenka (advisor)
Concrete has many advantageous properties as regards resistance to fire. It is non-flammable and it has a low thermal conductivity. However, concrete structures, which are not designed for resistance against fire, show significant damage after heating. In particular, the explosive flaking with the consequence of weakening the reinforced concrete cross-section and exposing the steel reinforcement to the temperatures higher than critical temperature of reinforcement. There are only a few possible measures of preventing or mitigating the effects temperature load used. Ways of protection can be divided into two systems: active and passive. Active systems are designed to ensure the greatest possible reduction of temperatures the concrete is exposed to. Passive systems directly resist to high temperatures and fire. Design of composition of concrete with the aim of higher resistance to exposition to high temperatures belongs among the passive systems. A part of the work focuses on summary searches of the problems of concrete and reinforced concrete structures exposed to high temperatures and fire. The goal of the work is defining requirements for cement matrix based composite material and its design ensuring the highest possible resistance to high temperatures or direct fire.
|
|
| |
|
|
Stress strain analysis of a synchronous generator
Majdič, Petr ; Donát, Martin (referee) ; Dušek, Daniel (advisor)
This master thesis deals with an impact of particular static and dynamic forces and temperature strain on horizontal synchronous generator. In connection with this, a stress distribution in construction and an assessment of security to terminal state of flexibility and weariness is being solved together with finding the most critical places on horizontal synchronous generator.
|
|
|
The development of fire-resistant repair mortars with fine-grained filler
Záruba, Jiří ; Gross,, Tomáš (referee) ; Bydžovský, Jiří (advisor)
The diploma thesis is focused on fire-resistant repair mortar with fine-grained filler. The aim of this work is the research and development of fine-grained Mortars resistant to high temperatures, which are characteristic at the beginning of the fire. The theoretical knowledge with subsequently realized laboratory verification was used. At-tention was paid to the masses based on the mixed binder comprising cement and blast furnace slag, respectively. high-temperature ash. Cellulose fibres were used as the dis-persed reinforcement. Two kinds of aggregate were assessed - fly ash agloporit and am-phibolite incl. combinations thereof. Laboratory tests were carried out via determination of basic material properties (density, strength, consistency, dimensional changes etc.) after exposure to extreme temperatures. A substantial part of the research was also study of different cooling conditions - slow and fast (water and air). Selected formulations were subjected to temperatures up to 1200 ° C. In the conclusion is selected several recipes that have been found to be optimal for continuing research on the basis of the results and findings.
|
|
|
Studying the behavior of concrete at high temperatures
Fiala, Jiří ; Sitek,, Libor (referee) ; Bodnárová, Lenka (advisor)
This thesis deals with the behavior of cement concrete at high temperature with a focus on the impact behavior of aggregate, cement type and polypropylene fiber reinforcement. The theoretical part describes the issue of cement concrete at high temperatures, especially processes in the cement matrix, aggregates and polypropylene fibers. Furthermore, theoretical part describes the selection of a suitable type of cement and aggregates in concrete exposed to high temperatures. In the experimental part was designed the concrete composition with various kinds different types of aggregates and two types of cements. The temperature stress of test samples was performed according to ISO standard temperature curve 834. Subsequently, was made the verification of the physic-mechanical properties such as changes in bulk density and compressive strength after heat load. Moreover, the surface appearance of samples after heat load was evaluated, especially the occurrence of samples, the crack width and explosive spalling. Mineralogical composition changes of prepared samples before and after heat load were observed via X-ray diffraction analysis. Finally, we made a photogrammetry on a test plates after heat load which defined the size of the area and depth of spalling concrete surface.
|
|
|
Behavior of concrete at high temperatures
Dvořáková, Michaela ; Bruckner,, Dipl Heinrich (referee) ; Bodnárová, Lenka (advisor)
The aim of this diploma thesis is to focus on the resistance of concrete exposed to high temperatures especially with focus of resistance against explosive spalling as well as clarifying the mode of action of various types of polypropylene fibres. The theoretical part is an introduction to the issues of explosive spalling, its mechanisms and majority influencing factors. Further description of the processes taking place in the structure of concrete under extreme thermal load, distribution and size of pores in concrete, thermal load, temperature-time curves and their applications, methods of elimination of negative behaviour of concrete exposed to thermal loading (passive and active methods), mode of action of polypropylene fibres and more is also included in the theoretical part. The main aim of experimental part is to verify the function of polypropylene fibers of various Melt Flow Indexes (MFI) and dosage. Primarily, the test samples with content of the PP-fibers are compared to the reference sample without fibers. Secondarily, the samples with standard PP-fibers (with MFI 25) with dosage 2.0 kg/m3 are compared to samples with modified PP-fiber (with MFI 2500) of dosage 0.9 kg/m3. Photogrammetric images were used for evaluation and comparison of spalled surfaces and its depth. Determination of the softening temperature and melting point of the modified and standard PP-fibers was made by using a high temperature microscope video. The second part of the experimental work was to define concrete permeability at different temperatures and pressures. Permeability was measured at temperatures of 20°C, 90°C, 150°C, 175°C, 200°C, 225°C and 250°C and at pressure of 0.2, 0.4 and 0.6 MPa.
|
|
|
Pile Foundations - Energy Piles
Hoza, Martin ; Leiter, Augustin (referee) ; Glisníková, Věra (advisor)
At a time when ecology and renewable energy sources come to the fore, the use of geothermal energy appears to be one of the suitable alternatives. The aim of this paper is to explain the function of ground source heat pumps, to mention factors affecting the efficiency of the system and discuss the technology of energy piles realization. This paper also focuses at risks associated with the soil temperature influencing and shows examples of realization.
|
|
|
Design of the office structure
Totková, Lucie ; Pinkas, Karel (referee) ; Klusáček, Ladislav (advisor)
This thesis deals with the design and assessment of the cooling reinforced concrete ceiling by EC2: Design of Concrete Structures. The introductory part is focused on selected type cooling ceiling system and its detailed description. The important part is dedicated to influence of water temperature on reinforced concrete ceiling structure. In this thesis is included calculation of internal forces, calculation of maximal deflection of the slab and its assessment of the puncture. This task is analysed using the software SCIA Engineer and ANSYS.
|