Fracture behavior of FeAlSi intermetallics
 Čech, J. ; Haušild, P. ; Karlík, M. ; Nová, K. ; Průša, F. ; Novák, P. ; Kopeček, Jaromír
The study is devoted to the intermetallic alloy FeAl20Si20 (wt.%) with the potential applications in high temperature aggressive environments. The samples of the same chemical composition were prepared by spark plasma sintering from the different mechanically alloyed powders (pure elements and pre-alloyed powders).
Úplný záznam
Mechanical properties of plasma sprayed layers of NiAl10 and NiAl40 on AZ91 alloy
 Kubatík, Tomáš František ; Brodil, R. ; Ctibor, Pavel ; Průša, F. ; Brožek, Vlastimil
In this work, plasma coatings of NiAl10 and NiAl40 on magnesium alloy AZ91 substrate were prepared by the hybrid plasma spraying system WSP®-H 500. The both plasma sprayed coatings of NiAl10 and NiAl40 have metallurgical bond. The thicknesses of microstructures in the cross-section of NiAl10 and NiAl40 plasma sprayed coatings prepared by 9 passes were 374 and 440 μm respectively. Adhesion test of plasma sprayed layers was performed using a modified ASTM C 633 standard. The tensile adhesion strength values are 24.7 MPa for NiAl10 coatings and 12.3 MPa for NiAl40 coatings. Abrasion resistance according to Slurry Abrasion Response (SAR) test of NiAl40 layers had similar values (0.12 g/cm2)in a comparison with the uncoated AZ91 (0.126 g/cm2). Layers NiAl10 had greater weight losses (0.175 g/cm2) than uncoated AZ91. Microhardness of plasma coating of NiAl40 is several times greater than microhardnesses of plasma coating of NiAl10 and uncoated substrate AZ91
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English