Preparation of calcium-aluminate phases
Ohaňka, Zdeněk ; Novotný, Radoslav (referee) ; Koplík, Jan (advisor)
This work focuses on the preparation of calcium aluminates by solid state synthesis and by sol-gel method. Phases prepared were monocalcium aluminate (CA), dodecacalcium heptaaluminate (C12A7), tricalcium aluminate (C3A) and calcium dialuminate (CA2). Two modifications of sol-gel method were used – the difference between them was in the addition of EDTA. Each method was closely described and results were compared according to the achieved purity of prepared phases. X-ray diffraction analysis was used to determine the purity of prepared calcium-aluminates.
|
|
Synthesis of foamed bioceramics for potential medical applications
Doboš, Petr ; Šoukal, František (referee) ; Palou, Martin (advisor)
Cílem práce byla příprava porézních vzorků HAP pro potenciálně medicínské aplikace. HAP byl připraven metodou sol-gel a precipitační. Vzorky HAP byly podrobeny analýze FTIR, XRD, SEM. Takto připravený HAP byl napěněn pomocí houbové metody s jasně definovanými póry a pomocí polymerního a skleněného expanzelu s různou distribucí a velikostí pórů. U výsledných napěněných vzorků byla vyhodnocena mikrostruktura a povrchová analýza pomocí SEM, zjištěna porozita pomocí Hg porozimetru a sledována bioaktivita in vitro v SBF. Byly zjištěny jasně definované makro, mezo a mikro póry při různé distribuci. U houbové metody pomocí sol-gel došlo k vytvoření jasně definovaných a pravidelných pórů s monodisperzní porozitou. Dominantní velikost póru byla stanovena v rozmezí 1–5 µm. Celková porozita byla stanovena na 63,5 % s celkovým povrchem 3,048 1 m/g. Precipitační metodou s polymerním expanzelem došlo k polydisperznímu rozložení pórů s třemi hlavními fázemi v rozmezí: 50–100 µm, 5–10 µm a 0,5–1 µm. Celková porozita byla stanovena na 67,6 % s celkovým povrchem 19,090 3 m/g. Bioaktivita výsledných napěněných vzorků in vitro byla sledována po dobu 7 dnů v připraveném SBF. Při napěnění sol-gel houbovou metodou nevznikla výsledná bioaktivní vrstva. U precipitační metody napěněné pomocí polymerního expanzelu vznikla nepravidelná bioaktivní vrstva. Výsledky byly naměřeny pomocí SEM analýzy.
|
|
Preparation of calcium-aluminate phases
Ohaňka, Zdeněk ; Novotný, Radoslav (referee) ; Koplík, Jan (advisor)
This work focuses on the preparation of calcium aluminates by solid state synthesis and by sol-gel method. Phases prepared were monocalcium aluminate (CA), dodecacalcium heptaaluminate (C12A7), tricalcium aluminate (C3A) and calcium dialuminate (CA2). Two modifications of sol-gel method were used – the difference between them was in the addition of EDTA. Each method was closely described and results were compared according to the achieved purity of prepared phases. X-ray diffraction analysis was used to determine the purity of prepared calcium-aluminates.
|
|
Synthesis of foamed bioceramics for potential medical applications
Doboš, Petr ; Šoukal, František (referee) ; Palou, Martin (advisor)
Cílem práce byla příprava porézních vzorků HAP pro potenciálně medicínské aplikace. HAP byl připraven metodou sol-gel a precipitační. Vzorky HAP byly podrobeny analýze FTIR, XRD, SEM. Takto připravený HAP byl napěněn pomocí houbové metody s jasně definovanými póry a pomocí polymerního a skleněného expanzelu s různou distribucí a velikostí pórů. U výsledných napěněných vzorků byla vyhodnocena mikrostruktura a povrchová analýza pomocí SEM, zjištěna porozita pomocí Hg porozimetru a sledována bioaktivita in vitro v SBF. Byly zjištěny jasně definované makro, mezo a mikro póry při různé distribuci. U houbové metody pomocí sol-gel došlo k vytvoření jasně definovaných a pravidelných pórů s monodisperzní porozitou. Dominantní velikost póru byla stanovena v rozmezí 1–5 µm. Celková porozita byla stanovena na 63,5 % s celkovým povrchem 3,048 1 m/g. Precipitační metodou s polymerním expanzelem došlo k polydisperznímu rozložení pórů s třemi hlavními fázemi v rozmezí: 50–100 µm, 5–10 µm a 0,5–1 µm. Celková porozita byla stanovena na 67,6 % s celkovým povrchem 19,090 3 m/g. Bioaktivita výsledných napěněných vzorků in vitro byla sledována po dobu 7 dnů v připraveném SBF. Při napěnění sol-gel houbovou metodou nevznikla výsledná bioaktivní vrstva. U precipitační metody napěněné pomocí polymerního expanzelu vznikla nepravidelná bioaktivní vrstva. Výsledky byly naměřeny pomocí SEM analýzy.
|