Catalytic synthesis of polyanilines
Bláha, Michal ; Vohlídal, Jiří (advisor) ; Omastová, Mária (referee) ; Trchová, Miroslava (referee)
This Ph.D. thesis is dealing with catalytic polymerization of aniline (ANI) and partially also of substituted anilines with FeCl3/H2O2 catalyst system, in which according to obtained results both active species, Fe3+ and HO , participate in the overall polymerization mechanism, creating a synergic system. The Fe3+ /H2O2 catalyst system, also called Fenton's system can considerably lower contamination of forming neat polyanilines (PANIs) by side-products characteristic of stoichiometric polymerization. However, catalytically prepared PANIs exhibit reduced conductivity related most probably to side reactions involving radicals generated as integral components of the FeCl3/H2O2 system. Catalytic polymerization of ANI with FeCl3/H2O2 system was found to be the reaction of approx. 2nd order with respect to ANI and gives PANIs of a good quality only when [H2O2] in the reaction mixture was kept low, i.e., at under- stoichiometric ratios [H2O2]/[ANI]. At over-stoichiometric ratio [H2O2]/[ANI], PANIs of lowered conductivity, worse spectroscopic characteristics and increased size of PANI nanostructures were obtained; nevertheless, these PANIs were not over-oxidized to pernigraniline state. The reaction-time profiles of the open-circuit potential of reaction mixtures exhibited an inflection related to the...
|
|
| |
|
|
The Study of the Molecular Structure of Various Forms of Conducting Polymers using FTIR and Raman Spectroscopies
Morávková, Zuzana ; Trchová, Miroslava (advisor) ; Baumruk, Vladimír (referee) ; Matějka, Pavel (referee)
In this Thesis, the structure of thin films formed by a conducting polymer, polyaniline, was studied using mainly infrared and Raman spectroscopies. That led to the study of aniline oligomers. The oligomers play a key role in the formation of thin films and nanostructures of polyaniline. Furthermore, the Thesis deals with the carbonization of various forms of polyaniline (granular polyaniline base, thin films of polyaniline salt, multi-wall carbon nanotubes coated with polyaniline salt or base, polyaniline nanotubes/nanorods prepared in the presence of ethanol). The two topics, aniline oligomers and carbonization of polyaniline, are connected by a paper concerning the carbonization of microspheres formed during oxidation of aniline in alkaline medium. Optical microscopy, transmission and scanning electron microscopy, UV-Vis spectroscopy, spectroscopic ellipsometry, wide angle X-ray scattering and thermogravimetric analysis were used.
|
|
|
Catalytic synthesis of polyanilines
Bláha, Michal ; Vohlídal, Jiří (advisor) ; Omastová, Mária (referee) ; Trchová, Miroslava (referee)
This Ph.D. thesis is dealing with catalytic polymerization of aniline (ANI) and partially also of substituted anilines with FeCl3/H2O2 catalyst system, in which according to obtained results both active species, Fe3+ and HO , participate in the overall polymerization mechanism, creating a synergic system. The Fe3+ /H2O2 catalyst system, also called Fenton's system can considerably lower contamination of forming neat polyanilines (PANIs) by side-products characteristic of stoichiometric polymerization. However, catalytically prepared PANIs exhibit reduced conductivity related most probably to side reactions involving radicals generated as integral components of the FeCl3/H2O2 system. Catalytic polymerization of ANI with FeCl3/H2O2 system was found to be the reaction of approx. 2nd order with respect to ANI and gives PANIs of a good quality only when [H2O2] in the reaction mixture was kept low, i.e., at under- stoichiometric ratios [H2O2]/[ANI]. At over-stoichiometric ratio [H2O2]/[ANI], PANIs of lowered conductivity, worse spectroscopic characteristics and increased size of PANI nanostructures were obtained; nevertheless, these PANIs were not over-oxidized to pernigraniline state. The reaction-time profiles of the open-circuit potential of reaction mixtures exhibited an inflection related to the...
|
|
| |
|
| |
guest ::