Original title: Modulace viskozity kafrem při stereolitografickém tisku pokročilých keramických materiálů
Translated title: Viscosity modulation by camphor during stereolithography printing of advanced ceramic materials
Authors: Sokola, Patrik ; Roleček, Jakub (referee) ; Salamon, David (advisor)
Document type: Bachelor's theses
Year: 2021
Language: slo
Publisher: Vysoké učení technické v Brně. Fakulta chemická
Abstract: [slo] [eng]
Táto bakalárska práca sa zaoberá prípravou tlačových suspenzií s obsahom keramiky, ich následnou tlačou a vyhodnotením vlastností spečenej keramiky. Pri príprave tlačovej suspenzie (s použitím zirkónového prášku stabilizovaného yttriom) bol skúmaný najmä vplyv modulátoru viskozity, konkrétne gáforu, na vlastnosti suspenzie a finálnu mikroštruktúru vytlačených a spečených objektov. Boli pripravené vzorky s rôznym obsahom keramických častíc a bol zisťovaný vplyv gáforu na reologické vlastnosti suspenzie. Bolo zistené, že gáfor má pozitívny vplyv na zníženie viskozity pri vybranom objemovom množstve keramiky a bolo indikované maximálne množstvo zirkónového prášku v epoxidovej živici, aby bola suspenzia použiteľná pre potreby stereolitografickej tlače. Po samotnej tlači bola vyhodnotená hustota vzoriek, ich porozita, veľkosť častíc, defekty v mikroštruktúre, vizuálna kvalita a percentuálne zmrštenie. Vzorky s gáforom vykazovali lepšie vlastnosti pre rôzne objemové obsahy zirkónovej keramiky pre všetky spomínané faktory. This bachelor's thesis deals with the preparation of printing suspensions containing ceramics, their subsequent printing and evaluation of the properties of sintered ceramics. In the preparation of the printing suspension using zirconium powder stabilized with yttrium, the influence of the viscosity modulator, in particular the camphor, on the properties of the suspension and the final microstructure of the extruded and sintered objects was investigated. Samples with different contents of ceramic particles were prepared and the effect of camphor on the rheological properties of the suspension was determined. It has been found that camphor always has a positive effect on reducing the viscosity of a selected volume of ceramic, and the maximum amount of zirconium powder in the epoxy resin has been determined to make the suspension usable for stereolithographic printing. After printing, the density of the samples, their porosity, particle size, defects in the microstructure, visual quality and percentage shrinkage were evaluated. The camphor samples showed better properties for different volumetric contents of zirconium ceramics for all the mentioned factors.
Keywords: 3D printing; ceramic suspension; microstructure; rheological behavior; zirconium ceramics

Institution: Brno University of Technology (web)
Document availability information: Fulltext is available in the Brno University of Technology Digital Library.
Original record: http://hdl.handle.net/11012/201341

Permalink: http://www.nusl.cz/ntk/nusl-576430


The record appears in these collections:
Universities and colleges > Public universities > Brno University of Technology
Academic theses (ETDs) > Bachelor's theses