Original title: Elektrochemické charakteristiky hořčíkových slitin AZ31 a AZ61 v Hankových roztocích
Translated title: Electrochemical characteristics of AZ31 and AZ61 magnesium alloys in Hanks‘ solutions
Authors: Minda, Jozef ; Wasserbauer, Jaromír (referee) ; Tkacz, Jakub (advisor)
Document type: Master’s theses
Year: 2015
Language: cze
Publisher: Vysoké učení technické v Brně. Fakulta chemická
Abstract: [cze] [eng]
Práca sa zaoberá elektrochemickou charakterizáciou koróznych vlastností perspektívnych materiálov, horčíkových zliatin pre biomedicínske aplikácie. Boli použité tvárnené zliatiny AZ31 a AZ61 a exponované koróznemu prostrediu Hankových roztokov (SBF) na simuláciu podmienok prostredia v živých organizmoch. Na hodnotenie povrchu bola využitá rastrovacia elektrónová mikroskopia (scanning electron microscopy, SEM) s prvkovou analýzou pomocí energiovo-disperznou spektroskopie (EDS). Boli vykonané krátkodobé (5 min) a dlhodobé (72 hod) korózne testy s cieľom optimalizovať metodiku merania a získať korózne parametre – predevšetkým koróznyí potenciál (Ekor), koróznu prúdovú hustotu (ikor), koróznu rýchlosť (vkor) a polarizační odpor (RP). Na vyhodnotenie krátkodobých testov boli využité potenciodynamické skúšky, konkrétne metóda lineárnej polarizácie (LP) a pre dlhodobé experimenty bola využitá metóda elektrochemickej impedančnej spektroskopie (EIS). Z nameraných výsledkov boli porovnané vplyvy zloženia zliatin (AZ31 a AZ61), povrchovej úpravy (brúsenie a leštenie) a zloženia roztoku (SBF bez obsahu Ca, Mg a s obsahom Ca, Mg). Bolo charakterizované komplexné korózne správanie v čase a diskutované možné korózne mechanizmy. This thesis deals with the characterization of electrochemical corrosion properties of magnesium alloys as promising materials for biomedical applications. The wrought alloys AZ31 and AZ61 were used and exposed to corrosive environments of Hanks solutions (SBF) to simulate environmental conditions in living organisms. For the evaluation of the surfaces was used scanning electron microscopy (SEM) with elemental analysis measured by energy-dispersive spectroscopy (EDS). Short-term (5 min) and long-term (72 h) corrosion tests were conducted in order to optimize the measurement methodology and obtain corrosion parameters - especially corrosion potential (Ekor), corrosion current density (ikor) and polarisation resistance (RP). To evaluation of the short-term tests were by potentiodynamic tests, namely the linear polarization (LP) test. Long-term tests were measured by electrochemical impedance spectroscopy (EIS). Effects of the composition of the alloys (AZ31 and AZ61), surface treatment (grinding and polishing) and the composition of the solution (SBF without Ca, Mg, and with Ca, Mg) were compared. Complex corrosion behaviour in time was characterized and corrosion mechanisms were discussed.
Keywords: electrochemical impedance spectroscopy; linear polarization; magnesium alloys; simulated body fluid; elektrochemická impedančná spektroskopia (EIS); Horčíkové zliatiny; lineárna polarizácia (LP); roztoky telových tekutín (SBF)

Institution: Brno University of Technology (web)
Document availability information: Fulltext is available in the Brno University of Technology Digital Library.
Original record: http://hdl.handle.net/11012/38296

Permalink: http://www.nusl.cz/ntk/nusl-543820


The record appears in these collections:
Universities and colleges > Public universities > Brno University of Technology
Academic theses (ETDs) > Master’s theses