Název:
Three-dimensionally ordered micromesoporous carbon as adsorbent for CO2 capture
Autoři: Vorokhta, Maryna ; Řimnáčová, Daniela ; Pilař, Radim
Typ dokumentu: Příspěvky z konference
Konference/Akce: International Conference on Chemical Technology /7./, Mikulov (CZ), 20190415
Rok: 2019
Jazyk: eng
Abstrakt: In this work, ordered three-dimensionally micromesoporous carbon composed of large spherical mesopores 13 nm in diameter and small micropores with a mean micropore width of 1.46 nm, connecting the main spheres, was synthesized and investigated for CO2 capture ability at temperatures of 25°C, 35°C and 50°C, and at pressures up to 6.5 MPa. Because of the big pore volume occupying 3.62 cm3/g, composed of mesopores and micropores, the carbon sample showed very high adsorption capacity at high pressures. The highest CO2 adsorption capacity of 24.03 mmol/g was obtained at 25°C and at 5.5 MPa. As the temperature increased, the CO2 adsorption capacity decreased to 13.34 mmol/g at 50°C and at 6.5 MPa. The Freundlich fittings of the measured adsorption isotherms at pressures up to 2 MPa showed very high correlation coefficients. The estimated isosteric heats of adsorption in the range of 5.62-6.90 kJ/mol indicated a physical adsorption process, and suggested a stronger interaction between CO2 molecules than between CO2 molecules and the surface of the carbon sample.
Klíčová slova: 3DOmm carbon; CO2 adsorption; Freundlich fit; Isosteric heat
Zdrojový dokument: Proceedings of the 7th International Conference on Chemical Technology, ISBN 978-80-88307-00-6
Instituce: Ústav struktury a mechaniky hornin AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný na externích webových stránkách.
Externí umístění souboru: https://www.icct.cz/AngiologyKlon-ICCT/media/system/2019/ICCT-2019-Proceedings.pdf
Původní záznam: http://hdl.handle.net/11104/0301504
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-407923
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav struktury a mechaniky hornin
Konferenční materiály > Příspěvky z konference
Autoři: Vorokhta, Maryna ; Řimnáčová, Daniela ; Pilař, Radim
Typ dokumentu: Příspěvky z konference
Konference/Akce: International Conference on Chemical Technology /7./, Mikulov (CZ), 20190415
Rok: 2019
Jazyk: eng
Abstrakt: In this work, ordered three-dimensionally micromesoporous carbon composed of large spherical mesopores 13 nm in diameter and small micropores with a mean micropore width of 1.46 nm, connecting the main spheres, was synthesized and investigated for CO2 capture ability at temperatures of 25°C, 35°C and 50°C, and at pressures up to 6.5 MPa. Because of the big pore volume occupying 3.62 cm3/g, composed of mesopores and micropores, the carbon sample showed very high adsorption capacity at high pressures. The highest CO2 adsorption capacity of 24.03 mmol/g was obtained at 25°C and at 5.5 MPa. As the temperature increased, the CO2 adsorption capacity decreased to 13.34 mmol/g at 50°C and at 6.5 MPa. The Freundlich fittings of the measured adsorption isotherms at pressures up to 2 MPa showed very high correlation coefficients. The estimated isosteric heats of adsorption in the range of 5.62-6.90 kJ/mol indicated a physical adsorption process, and suggested a stronger interaction between CO2 molecules than between CO2 molecules and the surface of the carbon sample.
Klíčová slova: 3DOmm carbon; CO2 adsorption; Freundlich fit; Isosteric heat
Zdrojový dokument: Proceedings of the 7th International Conference on Chemical Technology, ISBN 978-80-88307-00-6
Instituce: Ústav struktury a mechaniky hornin AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný na externích webových stránkách.
Externí umístění souboru: https://www.icct.cz/AngiologyKlon-ICCT/media/system/2019/ICCT-2019-Proceedings.pdf
Původní záznam: http://hdl.handle.net/11104/0301504
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-407923
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav struktury a mechaniky hornin
Konferenční materiály > Příspěvky z konference
Záznam vytvořen dne 2019-11-25, naposledy upraven 2023-12-06.