Název: Struktura a mechanické vlastnosti nástřiku Ti-6Al-4V připraveného metodou Cold Spray
Překlad názvu: Strucure and mechnical properties of cold sprayed Ti-6Al-4V layer
Autoři: Sabela, Jakub ; Zelený, Martin (oponent) ; Řehořek, Lukáš (vedoucí práce)
Typ dokumentu: Diplomové práce
Rok: 2019
Jazyk: slo
Nakladatel: Vysoké učení technické v Brně. Fakulta strojního inženýrství
Abstrakt: [slo] [eng]
Diplomová práca sa v prvej časti zaoberá súčasným stavom poznania problematiky cold spray, jej mechanizmom a parametrami depozície, pokročilými povlakmi zhotovenými metódou cold spray, aplikáciami povlakov zhotovených touto metódou a poznatkami titánových a Ti-6Al-4V povlakov a ich tepelným spracovaním. Metódou cold spray bol vyrobený depozit prášku Ti-6Al-4V. V experimentálnej časti bola pozorovaná a skúmaná mikroštruktúra a mechanické vlastnosti dodaného stavu a jeho tepelne spracovaných stavov. Žíhaním pri 600 °C ostali mechanické vlastnosti a mikroštruktúra rovnaké ako v prípade dodaného materiálu. Žíhaním pri 800 °C sa rekryštalizovala mikroštruktúra a fáze za vzniku zrnitej mikroštruktúry a došlo k poklesu mechanických vlastností. Žíhaním pri 900 °C sa zlepšili mechanické vlastnosti vďaka zakaleniu mikroštruktúry, ktorá pozostáva z a ’ fázy. Žíhaním pri 1000 °C zhrublo zrno a klesli mechanické vlastnosti. Najlepšie vlastnosti z hľadiska mikroštruktúry a mechanických vlastností mal materiál žíhaný pri 800 °C, kalený a precipitačne precipitačne vytvrdený. Diploma thesis deals in the first part with recent knowledge of cold spray, its mechanism and parameters of deposition, advanced coatings made by cold spray and their applications, knowledge of Ti-6Al-4V coatings and their heat treatment. Deposit of Ti- 6Al-4V powder was made by cold spray process. In experimental part, microstructure and mechanical properties of supplied and its heat treated material were observed and examined. Mechanical properties and microstructure remained unchanged by annealing at 600 °C as in the case of supplied material. Recrystallization occured in microstructure of and phases by annealing at 800 °C. Grains were emerged in microstructure and mechanical properties were decreased. Mechanical properties were improved by annealing at 900 °C due to quenching. Microstructure consists of and ’ phases. Mechanical properties were the worst for annealed material at 1000 °C because of coarsed grains. Material which was annealed at 800 °C, quenched and precipitation hardened had the best microstructure and mechanical properties.
Klíčová slova: adiabatic shear instability; Cold spray; deposition; heat treatment.

Instituce: Vysoké učení technické v Brně (web)
Informace o dostupnosti dokumentu: Plný text je dostupný v Digitální knihovně VUT.
Původní záznam: http://hdl.handle.net/11012/175551

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-400850


Záznam je zařazen do těchto sbírek:
Školství > Veřejné vysoké školy > Vysoké učení technické v Brně
Vysokoškolské kvalifikační práce > Diplomové práce