Název: Combined coatings against mechanical wear and corrosion low carbon steel
Autoři: Brožek, Vlastimil ; Pokorný, P. ; Kolísko, J. ; Vokáč, M. ; Mastný, L. ; Stoulil, J.
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2017: International Conference on Metallurgy and Materials /26./, Brno (CZ), 20170524
Rok: 2017
Jazyk: eng
Abstrakt: In this study, special ceramic coatings were prepared on low carbon steel (1.0060 - EN 10027-2) via the plasma spraying technique using a WSP®-H plasma generator with output of up to 40 kg/h of aluminum oxide. Corundum coatings were deposited directly on the surface of steel plungers equipped with an anti-corrosion interlayer of zinc phosphate. Coating adhesion properties were tested using pin-off tests (modified ISO 4624) and reached a maximum value of 26 MPa. Corrosion resistance was evaluated by measurements of impedance spectra in the 100 kHz - 10 mHz range in a water solution of sodium sulfate. The capacity of electric double-layer varied depending on the porosity and thickness of the coating. Low-porosity coatings of >1.5 mm thickness had RCT 1.29·105 Ω·m2. The abrasive resistance of coatings was measured by rotary/machining test with SiC cutting knives, using a downforce of 50 kg·cm-2. Abrasion losses decreased with the quality of finish - starting at 0.00266 g cm-2 min-1 down to virtually zero losses after polishing the surface below Ra = 0.55 micro m.
Klíčová slova: Abrasion; Ceramic coatings; Corrosion resistance; Plasma spraying; Steel phosphating
Zdrojový dokument: METAL 2017 - 26th International Conference on Metallurgy and Materials, Conference Proceedings, ISBN 978-80-87294-79-6

Instituce: Ústav fyziky plazmatu AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0284209

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-375637


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky plazmatu
Konferenční materiály > Příspěvky z konference