Short-circuit diffusion of 99Mo in partly crystallized Fe76Mo8Cu1B15, Fe40Ni40B20 and Fe80B20 alloys
Překlad názvu:
Difúze po 99Mo po rychlý drahách v částečně krystalizovaných slitinách Fe76Mo8Cu1B15, Fe40Ni40B20 a Fe80B20
Autoři:
Čermák, Jiří ; Stloukal, Ivo ; Schneeweiss, Oldřich Typ dokumentu: Příspěvky z konference Konference/Akce: NANO ´05, Brno (CZ), 2005-11-08 / 2005-11-10
Rok:
2005
Jazyk:
eng
Abstrakt: [eng][cze] Self-diffusion of 99Mo in three chosen alloys that belong to NANOPERM – type family was studied. The measurement of penetration profiles was carried out by serial sectioning method combined with Ar+ ion beam sputtering technique in the temperature interval 548 – 648 K. Diffusion characteristics in all three experimental materials were measured in as quenched state and in a state after two different pre-annealing treatments: 683 K / 1 h and 743 K / 1 h. It was found that diffusion is controlled by two diffusion mechanisms and that the faster one is sensitive to pre-treatment of the alloy.Byla studsována autodifúze 99Mo ve třech vybraných slitinách patřících do rodiny typu NANOPERM. Pro měření penetračních profilů bylo použito metody odebírání vrstev kombinované s odprašovaním Ar+ ionty v teplotním intervalu 548 - 648 K. Difpzní chcrakteristiky ve všech třech slitinách byly měřany v litém stavu a ve dvou stavech po tepelném zpracování. Bylo zjištěno, že difúze je řízena dvěma mechanismy, z nichž ten rycghlejší je citlivější na tepelné zpracování.
Klíčová slova:
amorphous materials; diffusion; nanocrystalline materials Číslo projektu: CEZ:AV0Z20410507 (CEP), GA106/04/0228 (CEP), IBS2041105 (CEP) Poskytovatel projektu: GA ČR, GA AV ČR Zdrojový dokument: Proceeding NANO '05, ISBN 80-214-3085-0