Original title: Fázové transformace ve slitinách na bázi Mg-Zn
Translated title: Phase transformations in Mg-Zn-based alloys
Authors: Fischer, Josef ; Stulíková, Ivana (advisor) ; Kekule, Tomáš (referee)
Document type: Master’s theses
Year: 2013
Language: cze
Abstract: In this thesis MgZnAlCa and MgZnAl materials were studied. For the study of phase transitions on studied materials the method of measuring the changes of resistivity and hardness was used. The measures were carried out at the temperature of 77 K and at the room temperature. Chosen annealing regimes were 20 K / 20 min and also regime without temperature change - 300 řC. Courses of annealing curves are similar. Material MgZnAlCa shows simpler course of annealing curves than material MgZnAl. With both materials the icosahedral quasicrystalis phase was observed. V této práci byly zkoumány materiály MgZnAlCa a MgZnAl. Pro studium fázových změn ve studovaných materiálech byla použita metoda měření změn rezistivity a tvrdosti. Měření probíhala při teplotě 77 K a při pokojové teplotě. Zvolené žíhací režimy byly 20 K / 20 min a dále režim bez změny teploty - 300 řC. Průběhy žíhacích křivek jsou podobné. Materiál MgZnAlCa vykazuje jednodušší průběh žíhacích křivek než materiál MgZnAl. V obou materiálech byla pozorována icosahedrální kvazikrystalická fáze.

Institution: Charles University Faculties (theses) (web)
Document availability information: Available in the Charles University Digital Repository.
Original record: http://hdl.handle.net/20.500.11956/51681

Permalink: http://www.nusl.cz/ntk/nusl-321002


The record appears in these collections:
Universities and colleges > Public universities > Charles University > Charles University Faculties (theses)
Academic theses (ETDs) > Master’s theses