Vliv substitucí na magnetokalorický jev u vybraných sloučenin vzácných zemin

Kaštil, Jiří

The anisotropy of the magnetocaloric effect was studied on DyNiAl single crystal. Our data reveal a strong anisotropy of the magnetocaloric effect. The large effect occurs for field applied along the c-axis whereas the entropy change is small for the perpendicular field direction. The influence of substitution on the magnetocaloric effect was measured in the Gd(Co1-xRhx)2 compounds (where x was from 0.05 to 0.30) and Dy(Co1-xFex)2 compounds (where x was from 0.00 to 0.03). The substitution of Co by Rh leads to a decrease of the transition temperature, Tc, and increase of the maximum entropy change. The Tc increases but the maximum of entropy change quickly decreases in case of Fe substitution. The last studied systems were the Gd1-xTbx alloys with x in range from 0.00 to 0.40. The influence of the sample shape and orientation was studied. The thin ribbon oriented along the magnetic filed gave the highest value of the entropy change. The three measurement techniques were used: the heat capacity measurement, the magnetization measurement and the direct measurement of the temperature change.

guest :: login Digital Repository
		Search		Submit		Help		About