Název:
METALLURGY AND PROPERTIES OF ADVANCED NiAl-Mo EUTECTICS
Autoři: Barták, Tomáš ; Kuchařová, Květa ; Záležák, Tomáš ; Dlouhý, Antonín
Typ dokumentu: Příspěvky z konference
Konference/Akce: Metal 2010. International Conference on Metallurgy and Materials /19./, Rožnov pod Radhoštěm (CZ), 2010-05-18 / 2010-05-20
Rok: 2010
Jazyk: eng
Abstrakt: A NiAl-Mo eutectic alloy was melt from 99,99% purity components and cast by the drop casting technique. The drop-cast ternary alloy (nominal composition of Ni-45Al-9Mo at. %), was re-melted and directionally solidified using a high temperature optical floating zone furnace. A resulting in-situ composite consists of Ni-45,2Al matrix and Mo-10Al-4Ni fibers, all in at. %. The volume fraction of 14% Mo-fibers stems from the eutectic composition. Backscatter diffraction shows that the NiAl-matrix and the Mo-fibers are both < 001 >-oriented with respect to the axis of the cylindrical rods. Preliminary creep experiments confirmed an immense improvement of high temperature strength due to the fine distribution of Mo-fibres. The amount of strengthening in terms of minimum creep rate can be as high as 7 orders of magnitude. Post-mortem transmission electron microscopy experiments provided evidence that creep in the temperature range of 800 - 900 degrees C results in an extensive formation of subgrain boundaries. The strengthening effect is very likely associated with the reactions between subgrain boundaries and fine Mo-fibres.
Klíčová slova: composite; directional solidification; eutectics
Číslo projektu: CEZ:AV0Z20410507 (CEP), GA202/09/2073 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: METAL 2010: 19TH INTERNATIONAL METALLURGICAL AND MATERIALS CONFERENCE, ISBN 978-80-87294-17-8
Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný na externích webových stránkách.
Externí umístění souboru: http://www.metal2014.com/files/proceedings/metal_10/lists/papers/175.pdf
Původní záznam: http://hdl.handle.net/11104/0243536
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-180626
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
Autoři: Barták, Tomáš ; Kuchařová, Květa ; Záležák, Tomáš ; Dlouhý, Antonín
Typ dokumentu: Příspěvky z konference
Konference/Akce: Metal 2010. International Conference on Metallurgy and Materials /19./, Rožnov pod Radhoštěm (CZ), 2010-05-18 / 2010-05-20
Rok: 2010
Jazyk: eng
Abstrakt: A NiAl-Mo eutectic alloy was melt from 99,99% purity components and cast by the drop casting technique. The drop-cast ternary alloy (nominal composition of Ni-45Al-9Mo at. %), was re-melted and directionally solidified using a high temperature optical floating zone furnace. A resulting in-situ composite consists of Ni-45,2Al matrix and Mo-10Al-4Ni fibers, all in at. %. The volume fraction of 14% Mo-fibers stems from the eutectic composition. Backscatter diffraction shows that the NiAl-matrix and the Mo-fibers are both < 001 >-oriented with respect to the axis of the cylindrical rods. Preliminary creep experiments confirmed an immense improvement of high temperature strength due to the fine distribution of Mo-fibres. The amount of strengthening in terms of minimum creep rate can be as high as 7 orders of magnitude. Post-mortem transmission electron microscopy experiments provided evidence that creep in the temperature range of 800 - 900 degrees C results in an extensive formation of subgrain boundaries. The strengthening effect is very likely associated with the reactions between subgrain boundaries and fine Mo-fibres.
Klíčová slova: composite; directional solidification; eutectics
Číslo projektu: CEZ:AV0Z20410507 (CEP), GA202/09/2073 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: METAL 2010: 19TH INTERNATIONAL METALLURGICAL AND MATERIALS CONFERENCE, ISBN 978-80-87294-17-8
Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný na externích webových stránkách.
Externí umístění souboru: http://www.metal2014.com/files/proceedings/metal_10/lists/papers/175.pdf
Původní záznam: http://hdl.handle.net/11104/0243536
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-180626
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
Záznam vytvořen dne 2015-02-02, naposledy upraven 2022-09-29.