Compressive Creep Tests of An Aluminium Powder Composite Reinforced by Ceramic Particles
 Dvořák, Jiří ; Král, Petr ; Balog, M. ; Simančík, F. ; Sklenička, Václav
The aim of this work is to study of a composite mixture of aluminium powders, to analyze of composite microstructure and mostly to describe the creep behaviour of composite in compression. The experimental material was based on Al powder matrix (Al 99%) about the particle size of less than 200 µm. This powder was mixtured with silicon carbide particles (SiC) having the size about 10 µm. The Al composite powder was prepared via conventional direct hot-extrusion (DE) at temperature 450°C. The microstructural investigations were performed using OM and SEM. It was found that DE process exhibits some breaking of carbide particles to size of range from 0.5 to 5 µm. Creep tests in compression were conducted at temperatures 423 -623 K and at applied stresses in the range from 60 to 100 MPa. Consequently, for an evaluation of controlling creep mechanisms an activation energy of creep and the stress exponent of the creep rate were determined.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English