Název: Corrosion of Nickel Exposed to LiF-NaF Molten Salt
Autoři: Král, Lubomír ; Čermák, Jiří ; Matal, O. ; Šimo, T. ; Nesvadba, L.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Anniversary International Conference on Metallurgy and Materials METAL 2011/20th./, Brno (CZ), 2011-05-18 / 2011-05-20
Rok: 2011
Jazyk: eng
Abstrakt: This work is devoted to study of changes of structure and chemical composition in corrosion areas of the chosen candidate alloy, Nickel 201, for components of a LS-VHTR. The material was annealed at 1013K/10h/vacuum and at 1000°C/24h/Ar before corrosion tests. The annealed material was studied after its exposure to the molten mixture of 60 mol. % LiF + 40 mol. % NaF at the temperature of 1013K. The exposition was carried out in a quasidynamic regime, which simulates real circulation of the coolant (a mixture of molten salts) in the piping. The structure of the alloy was studied by SEM. Severe corrosion damage was observed in grain boundaries.
Klíčová slova: corrosion; LiF–NaF; molten salts; nickel
Číslo projektu: CEZ:AV0Z20410507 (CEP), 2A-1TP1/067 (CEP)
Poskytovatel projektu: GA MPO
Zdrojový dokument: METAL 2011 Conference Proceedings, ISBN 978-80-87294-22-2

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0006748

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-80959


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference