Original title: The investigation of an Al-Zr-Ti alloy prepared by spark plasma sintering of atomized powder
Authors: Molnárová, O. ; Málek, P. ; Lukáč, František ; Chráska, Tomáš ; Cinert, Jakub
Document type: Papers
Conference/Event: 26th International Conference on Metallurgy and Materials, Brno (CZ), 20170524
Year: 2017
Language: eng
Abstract: The microstructure and mechanical properties of a powder metallurgical Al-Zr-Ti alloy was studied. Fine powder with a typical size below 50 ?m was prepared by gas atomization. The smallest powder particles with a diameter below 10 ?m exhibited a segregation free microstructure. Larger droplets were found to contain intermetallic particles rich in Zr and Ti. The gas atomized powder was consolidated by spark plasma sintering (SPS) at various temperatures ranging from 450 to 550 °C. During SPS the materials microstructure remained nearly unchanged and a fine grain size between 2 and 3 ?m was observed. All SPS samples exhibited a microhardness of around 90 HV. The annealing (1 h, 500 °C) of the sample sintered at the highest temperature (550 °C) resulted in a decrease of microhardness to 75 HV as a result of changes in the phase composition, the fine grain size was retained. Natural aging at room temperature was not observed.
Keywords: Gas atomization; High strength alloy; Spark plasma sintering; Thermal stability
Project no.: GA15-15609S (CEP)
Funding provider: GA ČR
Host item entry: METAL 2017. 26th International Conference on Metallurgy and Materials. Conference Proceedings, ISBN 978-80-87294-79-6

Institution: Institute of Plasma Physics AS ČR (web)
Document availability information: Fulltext is available at the institute of the Academy of Sciences.
Original record: http://hdl.handle.net/11104/0295560

Permalink: http://www.nusl.cz/ntk/nusl-394149


The record appears in these collections:
Research > Institutes ASCR > Institute of Plasma Physics
Conference materials > Papers
 Record created 2019-04-15, last modified 2019-04-15


No fulltext
  • Export as DC, NUŠL, RIS
  • Share