Original title: Příprava a charakterizace Ni-P povlaku na lité hořčíkové slitině AZ91
Translated title: Preparation and characterization of Ni-P coating on AZ91 cast magnesium alloy
Authors: Brescher, Roman ; Buchtík, Martin (referee) ; Wasserbauer, Jaromír (advisor)
Document type: Bachelor's theses
Year: 2018
Language: cze
Publisher: Vysoké učení technické v Brně. Fakulta chemická
Abstract: [cze] [eng]
Táto bakalárska práca sa zaoberá bezprúdovou depozíciou nikel-fosforovej (Ni-P) vrstvy na horčíkovej zliatine AZ91. V úvode teoretickej časti sú zhrnuté základné poznatky o zliatinách horčíku so zameraním na zliatinu AZ91, vplyve použitých legujúcich prvkov a nečistôt a o jej mikroštruktúre. Teoretická časť pokračuje pojednaním o Ni-P povlaku so zameraním na zloženie kúpeľa, vplyve a účinku jeho jednotlivých zložiek. Ďalej sa v tejto časti nachádza porovnanie s galvanickým niklovaním. Na záver teoretickej časti bol zhrnutý súčasný výskum použitia bezprúdovej depozície Ni-P vrstvy na horčíkovej zliatine AZ91. V praktickej časti bol pripravený Ni-P povlak na horčíkovej zliatine AZ91, pozorovaná mikroštruktúra horčíkovej zliatiny a Ni-P vrstvy, zmeraná rýchlosť depozície, hrúbka, mikrotvrdosť a zloženie povlaku. Taktiež bol pozorovaný vplyv jeho tepelného vytvrdenia. Zistilo sa, že je možné pripraviť kvalitný Ni-P povlak na horčíkovej zliatine AZ91, ktorý bol bez viditeľných defektov, alebo zjavných nežiadúcich medzivrstiev, avšak tepelným vytvrdením povlaku dochádza k jeho praskaniu. Na stanovenie koróznej odolnosti bolo vykonané potenciodynamické meranie, výsledkom ktorého bolo zistenie, že nevytvrdený Ni-P povlak predstavuje vhodnú protikoróznu ochranu. Avšak tepelným vytvrdením sa korózna odolnosť vplyvom popraskania povrchu zhoršila až na úroveň čistej zliatiny AZ91. This bachelor thesis deals with electroless deposition of nickel-phosphoric (Ni-P) coating on AZ91 magnesium alloy. At the beginning of the theoretical part, there is a summary of basic knowledge about magnesium alloys with focus on AZ91 alloy and the influence of alloying elements and impurities and its microstructure. The theoretical part continues with the discussion of the Ni-P coating, focusing on the composition of the bath, the influence and the effect of its individual components. Next, there is a comparison with galvanic nickeling. At the end of the theoretical part, the current research of the use of electroless deposition of Ni-P layer on AZ91 magnesium alloy is summarized. In the practical part, there is the preparation of the Ni-P coating on the AZ91 magnesium alloy, the observation the microstructure of the magnesium alloy and the Ni-P layer, and rate of deposition, the thickness, the microhardness and the composition of the coating was measured. The effect of its heat treatment was also observed. It has been found that it is possible to produce a high-quality Ni-P coating on an AZ91 magnesium alloy which has no visible defects or obvious undesirable interlayers, however the heat treatment of the coating causes its cracking. To determine the corrosion resistance, a potentiodynamic measurement was performed, resulting in the finding that the Ni-P coating without heat treatment was a suitable corrosion protection. However, after heat treatment, the corrosion resistance due to cracking of the surface deteriorated to a level of bare AZ91 alloy.
Keywords: AZ91; electroless nickel; heat treatment of Ni-P; magnesium alloys; microhardness; potentiodynamic test; structure; AZ91; chemický nikel; horčíkové zliatiny; mikrotvrdosť; potenciodynamický test; tepelné vytvrdenie Ni-P; štruktúra

Institution: Brno University of Technology (web)
Document availability information: Fulltext is available in the Brno University of Technology Digital Library.
Original record: http://hdl.handle.net/11012/81972

Permalink: http://www.nusl.cz/ntk/nusl-378070


The record appears in these collections:
Universities and colleges > Public universities > Brno University of Technology
Academic theses (ETDs) > Bachelor's theses