Název: Comparison of calibration functions for short edge cracks under selected loads
Autoři: Seitl, Stanislav ; Miarka, Petr ; Malíková, Lucie ; Krejsa, M.
Typ dokumentu: Příspěvky z konference
Konference/Akce: FDM 2017 International Conference on Fracture and Damage Mechanics /16./, Florence (IT), 20170718
Rok: 2017
Jazyk: eng
Abstrakt: Attention to the fatigue cracks in steel structures and bridges has been paid for long time. In spite to efforts to eliminate the creation and propagation of fatigue cracks throughout the designed service life, cracks are still revealed during inspections. Note, that depending on location of initial crack, the crack may propagate from the edge or from the surface. The theoretical model of fatigue crack progression is based on linear fracture mechanics. Steel specimens are subjected to various load (tension, three- and four-point bending, pure bending etc.). The calibration functions for short edge cracks are compared for various load and the discrepancies are discussed.
Klíčová slova: Calibration curve; Edge crack; Fracture mechanics; Paris-erdogan law; Stress intensity factors
Číslo projektu: GA17-01589S (CEP)
Zdrojový dokument: Advances in Fracture and Damage Mechanics XVI, ISBN 978-3-0357-1168-4, ISSN 1662-9795

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0275685

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-373478


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
 Záznam vytvořen dne 2018-03-09, naposledy upraven 2018-03-09.


Není přiložen dokument
  • Exportovat ve formátu DC, NUŠL, RIS
  • Sdílet