Název: Cracking of ferritic stainless steel tubes during production process
Autoři: Majtás, Dušan ; Kreislová, K. ; Viani, Alberto ; Pérez-Estébanez, Marta ; Geiplová, H.
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2015. 24th International conference on metallurgy and materials, Brno (CZ), 20150603
Rok: 2015
Jazyk: eng
Abstrakt: From the economic reasons many products originally made from austenite stainless steel are nowadays made from ferritic stainless steel. Ferritic steels have relatively low yield strength and the work hardening is limited. They cannot be hardened by heat treatment and only moderately hardened by cold working. Commercially made stainless steel tubes from ferritic steel, used for industrial plumbing was examined on presence of cracks. The cracking was present on the inner side of the convoluted tube shape. The tube manufacturing process consisted of continual bending of the sheet to tube shape, weld the tube, then of cold shaping by pulling through rib-forming frames, which is done in several steps. Then thermal treatment applies to the nearly finished product to remove stress remaining in the structure. Prime suspect was deformation beyond the ductility of used material. However the stress-strain tensile testing does not approved this hypothesis. Several samples of failed material were taken together with reference, and were examined by optical microscopy, and X-Ray Diffraction structure analysis. The structure of the cracked tubes does not show the signs of deformation over the limit, except the location near to the crack itself. Interestingly enough the failed material showed more homogenous structure than the original one. Needle like structures were found when the material is “overetched”, on these structures concentration of stress under bending occur. This structure was identified as δ-ferrite, however its presence in α-ferrite matrix is unclear.
Klíčová slova: crystallographic defects; delta ferrite; mechanical failure; metallography
Číslo projektu: LO1219 (CEP)
Poskytovatel projektu: GA MŠk
Zdrojový dokument: METAL 2015. Conference proceedings, ISBN 978-80-87294-62-8

Instituce: Ústav teoretické a aplikované mechaniky AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0256341

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-202366


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav teoretické a aplikované mechaniky
Konferenční materiály > Příspěvky z konference