Effect of pH of mixing water on hydration and mechanical properties of cement composites.
Bezděk, Ondřej ; Krátký, Josef (referee) ; Šiler, Pavel (advisor)
This master’s thesis is focused on the effect of mixing water pH value on hydration and mechanical properties of cement composites based on portland cement. Source material was CEM I 42,5 R. Hydration process was analyzed by isoperibolic calorimetry, X-ray diffraction analysis and differential thermal analysis. Compressive and flexural strength was examined as mechanical properties. The samples microstructure was observed by scanning electron microscopy. Influence of mixing water pH value on flexural and compressive strength, retardation of hydration and ratio of individual phases was shown.
|
|
|
The influence of zinc oxide on the cement composite with silica fume.
Dobiáš, Jiří ; Koutný, Ondřej (referee) ; Šiler, Pavel (advisor)
The aim of this work was to investigate the influence of zinc oxide on the properties of blended Portland cement mixed with silica fume. On the pastes were monitored flow properties and by using of isoperibolic calorimetry process of the hydration. On the prepared samples were studied mechanical properties of obtaining values of compressive and flexural strength after 1, 7 and 28 days. By using of XRD were measured phase composition and microstructure development war observed by SEM. The elemental composition of cement leaches was measured by using of ICP-OES.
|
|
|
The influence of hydration accelerators on cement doped with zinc
Beneš, Pavel ; Šilerová,, Iva (referee) ; Šiler, Pavel (advisor)
Zinc in cement has negative properties mainly due to a significant delay in hydration. This bachelor thesis deals with the study of hydration of cements containing zinc. The course of cement hydration was monitored by isoperibolic calorimetry. Zinc was doped to CEM I 42.5 R in the form of 1 weight percent zinc oxide. Calcium oxide, formic acid and calcium formate were used in various proportions as accelerators. The obtained results were compared with the measured strengths and finally the suitability of the given accelerators was discussed for use in construction application.
|
|
|
Influence of zinc on mechanical properties of cement composites
Štarha, Tomáš ; Šilerová,, Iva (referee) ; Šiler, Pavel (advisor)
The theme of this bachelor thesis is to monitor the effect of zinc on mechanical properties of portland cement. Zinc was tested in the form of zinc oxide. Three acceleration additives were added, calcium oxide, formic acid and calcium formate in various proportions. Furthermore, the mechanical properties of all these mixtures were monitored by measuring flexural strength and compressive strength at 7 and 28 days after mixing and mixtures were analyzed by XRD and DTA. Also using isoperibolic calorimetry, the hydration of CEM 42.5 R cement zinc oxide was monitored.
|
|
|
The influence of aggregate on the properties of high performance concrete.
Bezděk, Ondřej ; Krátký, Josef (referee) ; Šiler, Pavel (advisor)
This bachelor thesis is focused on the influence of aggregates on the mechanical properties of high-performance concrete. The flexural strenght and the compressive strenght were observed after 1, 7 and 28 days. The process of hydratation was monitored using isoperibolic calorimetry. Laser particle size analysis of aggregates was also performed. As materials were used: Portland cement CEM I 42,5 R-Sc Mokrá, finelly ground silica sand, calcinated bauxite, fine test sand ČSN EN 196-1, medium test sand ČSN EN 196-1, rough test sand ČSN EN 196-1 and polycarboxylate superplasticizer Glenium Ace 40.
|
|
|
Influence of hydration accelerators on zinc - doped cement mortars
Beneš, Pavel ; Šilerová, Iva (referee) ; Šiler, Pavel (advisor)
This work deals with monitoring the hydration of cement mortars and cement pastes made from CEM I 42.5 R cement doped with zinc oxide in an amount of 1 % wt. To eliminate the delay in the onset of hydration due to the presence of zinc oxide, the following accelerators were added to the cement mixtures in different proportions: calcium oxide, formic acids and calcium formate. Hydration was monitored using isoperibolic calorimetry. Furthermore, the mechanical properties of mixtures were investigated, namely the tensile strength after bending and the compressive strength after 7 days and after 28 days. The cement mortars were further subjected to additional analyses, such as porosimetry, DTA/TG and SEM.
|
|
|
Influence of zinc on mechanical properties of cement composites
Štarha, Tomáš ; Šilerová,, Iva (referee) ; Šiler, Pavel (advisor)
The theme of this bachelor thesis is to monitor the effect of zinc on mechanical properties of portland cement. Zinc was tested in the form of zinc oxide. Three acceleration additives were added, calcium oxide, formic acid and calcium formate in various proportions. Furthermore, the mechanical properties of all these mixtures were monitored by measuring flexural strength and compressive strength at 7 and 28 days after mixing and mixtures were analyzed by XRD and DTA. Also using isoperibolic calorimetry, the hydration of CEM 42.5 R cement zinc oxide was monitored.
|
|
|
The influence of hydration accelerators on cement doped with zinc
Beneš, Pavel ; Šilerová,, Iva (referee) ; Šiler, Pavel (advisor)
Zinc in cement has negative properties mainly due to a significant delay in hydration. This bachelor thesis deals with the study of hydration of cements containing zinc. The course of cement hydration was monitored by isoperibolic calorimetry. Zinc was doped to CEM I 42.5 R in the form of 1 weight percent zinc oxide. Calcium oxide, formic acid and calcium formate were used in various proportions as accelerators. The obtained results were compared with the measured strengths and finally the suitability of the given accelerators was discussed for use in construction application.
|
|
|
The influence of zinc oxide on the cement composite with silica fume.
Dobiáš, Jiří ; Koutný, Ondřej (referee) ; Šiler, Pavel (advisor)
The aim of this work was to investigate the influence of zinc oxide on the properties of blended Portland cement mixed with silica fume. On the pastes were monitored flow properties and by using of isoperibolic calorimetry process of the hydration. On the prepared samples were studied mechanical properties of obtaining values of compressive and flexural strength after 1, 7 and 28 days. By using of XRD were measured phase composition and microstructure development war observed by SEM. The elemental composition of cement leaches was measured by using of ICP-OES.
|
|
|
Effect of pH of mixing water on hydration and mechanical properties of cement composites.
Bezděk, Ondřej ; Krátký, Josef (referee) ; Šiler, Pavel (advisor)
This master’s thesis is focused on the effect of mixing water pH value on hydration and mechanical properties of cement composites based on portland cement. Source material was CEM I 42,5 R. Hydration process was analyzed by isoperibolic calorimetry, X-ray diffraction analysis and differential thermal analysis. Compressive and flexural strength was examined as mechanical properties. The samples microstructure was observed by scanning electron microscopy. Influence of mixing water pH value on flexural and compressive strength, retardation of hydration and ratio of individual phases was shown.
|