Tin dioxide based semiconducting gas sensors
Gablech, Imrich ; Pytlíček, Zdeněk (referee) ; Prášek, Jan (advisor)
This project is aimed at semiconductive gas sensors based on tin dioxide. In the first part, gas sensors are divided depending on their principal of functionality. Next part is about functionality of tin dioxide gas sensors and the possibilities of active layer modification. Experimental describes gas sensor from its drawing until construction, testing and characterization. Several microelectronic technologies such as thin-film, thick-film, LTCC, spray-coating or wire-bonding were used for constructing the sensor. In the last part properties of gas sensors and differences in functionality between modified and unmodified gas sensor are summarized.
|
|
|
Fabrication of transparent oxidic conducting coatings by material printing
Žáková, Michaela ; Krystiník,, Pavel (referee) ; Dzik, Petr (advisor)
Thin transparent conductive layers containing ATO nanoparticles are a modern material that has found use in a wide range of optoelectronic applications. For liquid phase deposition there were designed and prepared compositions using a „brick and mortar“ approach combined templating agents. A sol-gel solution formed of inorganic precursors of tin chloride and antimony trichloride in the presence of ATO nanoparticles was mixed with a surfactant to improve the structure and wettability of applied films. Polyethylene glycol, polyoxyethylene (20)cetylether, sodium dioctylsulfosuccinate and polyvinylpyrrolidone were used as templating agents. Thin layers of these compositions were applied by the spin-coating method. Characterized parameters were resistivity, thickness and turbidity. A resul compositions showed relatively good electrical properties and high transparency and a potencial to be used for material printing.
|
|
|
Transparent conducting tin oxide layers prepared from inorganic precursors
Dvorský, Vojtěch ; Drbohlavová, Jana (referee) ; Dzik, Petr (advisor)
The thesis focuses on the preparation of transparent electrically conductive tin oxide layers. First, a stock sol based on inorganic precursors was synthetized. Substrates were coated with a small amount of sol by spin coating or material printing to form thin layers. By modifying the solution by adding additional substances, specific coating compositions were prepared to optimize the deposition and the resulting layer properties. Selected samples were analysed by mechanical profilometry, XRD, SEM and XPS.
|
|
|
Printed transparent oxide conductors
Bartoš, Radim ; Pekárková, Jana (referee) ; Dzik, Petr (advisor)
Thin films of tin oxide doped by fluorine or antimony were prepared by spincoating technique and material printing technique. Plenty of inorganic and organic coumpouds were used as precursors of fluorine and antimony. Sheet resistence of films were measured by 4-probe method and film thickness were determined by contact profilometer. Films were analyzed by Xray diffraction (XRD) and scan electron microscopy (SEM).
|
|
|
Fabrication and characterization of oxidic conductive layers
Bartoš, Radim ; Gemeiner,, Pavol (referee) ; Dzik, Petr (advisor)
Liquid composition for antimony doped tin oxide solgel deposition was prepared. Anorganic precursors of tin and antimony were used (tin(IV) chloride, antimony(III) chloride). ATO nanoparticles were dispergated in composition. This composition was used for spincoating deposition of thin films. Composition was analyzed by thermal analysis TGA and DSC. Sheet resistence of prepared samples were examined by four probe sensing. RMS roughness and thickness was measured by profilometry. Samples were analyzed by scan electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Transmittance and haze were measured and calculated by UV-VIS spektrometry with integration sphere.
|
|
|
Fabrication of transparent oxidic conducting coatings by material printing
Žáková, Michaela ; Krystiník,, Pavel (referee) ; Dzik, Petr (advisor)
Thin transparent conductive layers containing ATO nanoparticles are a modern material that has found use in a wide range of optoelectronic applications. For liquid phase deposition there were designed and prepared compositions using a „brick and mortar“ approach combined templating agents. A sol-gel solution formed of inorganic precursors of tin chloride and antimony trichloride in the presence of ATO nanoparticles was mixed with a surfactant to improve the structure and wettability of applied films. Polyethylene glycol, polyoxyethylene (20)cetylether, sodium dioctylsulfosuccinate and polyvinylpyrrolidone were used as templating agents. Thin layers of these compositions were applied by the spin-coating method. Characterized parameters were resistivity, thickness and turbidity. A resul compositions showed relatively good electrical properties and high transparency and a potencial to be used for material printing.
|
|
|
Fabrication and characterization of oxidic conductive layers
Bartoš, Radim ; Gemeiner,, Pavol (referee) ; Dzik, Petr (advisor)
Liquid composition for antimony doped tin oxide solgel deposition was prepared. Anorganic precursors of tin and antimony were used (tin(IV) chloride, antimony(III) chloride). ATO nanoparticles were dispergated in composition. This composition was used for spincoating deposition of thin films. Composition was analyzed by thermal analysis TGA and DSC. Sheet resistence of prepared samples were examined by four probe sensing. RMS roughness and thickness was measured by profilometry. Samples were analyzed by scan electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Transmittance and haze were measured and calculated by UV-VIS spektrometry with integration sphere.
|
|
|
Printed transparent oxide conductors
Bartoš, Radim ; Pekárková, Jana (referee) ; Dzik, Petr (advisor)
Thin films of tin oxide doped by fluorine or antimony were prepared by spincoating technique and material printing technique. Plenty of inorganic and organic coumpouds were used as precursors of fluorine and antimony. Sheet resistence of films were measured by 4-probe method and film thickness were determined by contact profilometer. Films were analyzed by Xray diffraction (XRD) and scan electron microscopy (SEM).
|
|
|
Transparent conducting tin oxide layers prepared from inorganic precursors
Dvorský, Vojtěch ; Drbohlavová, Jana (referee) ; Dzik, Petr (advisor)
The thesis focuses on the preparation of transparent electrically conductive tin oxide layers. First, a stock sol based on inorganic precursors was synthetized. Substrates were coated with a small amount of sol by spin coating or material printing to form thin layers. By modifying the solution by adding additional substances, specific coating compositions were prepared to optimize the deposition and the resulting layer properties. Selected samples were analysed by mechanical profilometry, XRD, SEM and XPS.
|
|
|
Tin dioxide based semiconducting gas sensors
Gablech, Imrich ; Pytlíček, Zdeněk (referee) ; Prášek, Jan (advisor)
This project is aimed at semiconductive gas sensors based on tin dioxide. In the first part, gas sensors are divided depending on their principal of functionality. Next part is about functionality of tin dioxide gas sensors and the possibilities of active layer modification. Experimental describes gas sensor from its drawing until construction, testing and characterization. Several microelectronic technologies such as thin-film, thick-film, LTCC, spray-coating or wire-bonding were used for constructing the sensor. In the last part properties of gas sensors and differences in functionality between modified and unmodified gas sensor are summarized.
|
guest ::