Mohelská, Lucie ; Wirthová, Michaela (referee) ; Opravil, Tomáš (advisor)
The work is studying posibilities of use secondary materials produced by energetical industry. In fact it studies posibilities of preparing supersulphates cements with secondary raw materials. Its main system for simulation was used milled portland clinker. To clinker were added diferent secondary raw materials from energetical industry with sulphate. On prepared samples were watched mechanical properties in time. Tested were different samples of secondary raw materials.
|
|
|
Gypsum free cements with retarded setting by plastisizer and alkali compond
Sedlařík, Tomáš ; Ptáček, Petr (referee) ; Havlica, Jaromír (advisor)
This thesis deals with preparation of gypsum free cements with retarded solidification. It focuses on their preparation by alkali activation with addition of superplasticizers and without superplasticizers. The main aim of this work is to suggest substitution of gypsum in Portland cement by other materials. Ash after fluidized combustion was chosen as a good compensatory raw material with respect to sustainable development. Milled fluidized bed ash from heating station Třinec was tested. Examined pastes were prepared by alkali activation. 50% solution NaOH and sodium water-glass were used as alkali activators. Trial specimens (20x20x100 mm) were prepared from pastes. Measurements of calorimetric properties of unprocessed pastes tested mixtures were implemented. Bending and compressive strength of pastes were also explored.
|
|
| |
|
| |
|
|
Supersulphates cements
Mohelská, Lucie ; Wirthová, Michaela (referee) ; Opravil, Tomáš (advisor)
The work is studying posibilities of use secondary materials produced by energetical industry. In fact it studies posibilities of preparing supersulphates cements with secondary raw materials. Its main system for simulation was used milled portland clinker. To clinker were added diferent secondary raw materials from energetical industry with sulphate. On prepared samples were watched mechanical properties in time. Tested were different samples of secondary raw materials.
|
|
|
Gypsum free cements with retarded setting by plastisizer and alkali compond
Sedlařík, Tomáš ; Ptáček, Petr (referee) ; Havlica, Jaromír (advisor)
This thesis deals with preparation of gypsum free cements with retarded solidification. It focuses on their preparation by alkali activation with addition of superplasticizers and without superplasticizers. The main aim of this work is to suggest substitution of gypsum in Portland cement by other materials. Ash after fluidized combustion was chosen as a good compensatory raw material with respect to sustainable development. Milled fluidized bed ash from heating station Třinec was tested. Examined pastes were prepared by alkali activation. 50% solution NaOH and sodium water-glass were used as alkali activators. Trial specimens (20x20x100 mm) were prepared from pastes. Measurements of calorimetric properties of unprocessed pastes tested mixtures were implemented. Bending and compressive strength of pastes were also explored.
|
|
| |