Casting of manganese steels and their use
Dufka, Martin ; Šenberger, Jaroslav (referee) ; Pernica, Vítězslav (advisor)
Austenitic manganese steel, often referred as Hadfield´s steel after its discoverer, has an irreplaceable place in foundry due to its specific properties. Due to local pressures and shocks, surface of castings is hardened, but the cast core retains its toughness. Thus, manganese steel is used for castings of highly stressed machine parts that are subject to abrasive wear. This bachelor thesis is concerned about methods of production, chemical composition, influence of some alloying elements on properties and structure of steel, heat treatment, material properties, reinforcement mechanisms and types of individual deformation reinforcements. Further attention is paid to the most frequent use of manganese castings in practice.
|
|
|
DEFORMATION BEHAVIOR OF NANO/MICRO REINFORCED PMMA
Recman, Lukáš ; Nezbedová, Eva (referee) ; Kučera, Jaroslav (referee) ; Jančář, Josef (advisor)
Práce sleduje vliv velikosti částic na elastický modul a deformační chování za mezí kluzu. Bylo pozorováno, že jak elastická oblast, tak oblast za mezí kluzu ukazuje silnou závislost chování na velikosti částic. Cílem této práce je korelovat experimentální data a teoretické předpoklady které bylo odvozeny pro deformační chování v elastické oblasti a v oblasti za mezí kluzu pro amorfní polymery a konkrétně pro PMMA. Vše je motivováno propojit zatím oddělené oblasti kontinuální mikromechaniky a diskrétní nanomechaniky. Deformační chovaní PMMA plněného nano a mikro plnivem bylo pozorováno v elastické a plastické oblasti. Byl zkoumán vliv velikosti částic na velikost modulu a deformačního zpevnění. Mechanizmus vyztužení je interpretován s použitím teorie imobilizace řetězců, nanočástice mají silný vliv na molekulární dynamiku a kinetiku zapletenin. Mým příspěvkem k tomuto tématu je ukázat výraznou závislost na mechanizmu vyztužení v závislosti na velikosti částic. A to jak pod teplotou skelného přechodu tak nad teplotou skelného přechodu. Ačkoli pro velikost modulu byla publikována značná množství dat, která byla následně i interpretována, vliv částic na deformační zpevnění je poskrovnu. Během elastické deformace je primární struktura materiálu neměnná, jedná se o elastickou deformaci, za mezí kluzu již toto neplatí a primární struktura je zde nevratně poškozena. Bylo ukázáno, že obsah nano částic vede ke zvýšení meze kluzu a vyššímu deformačnímu zpevnění. Tento nárůst deformačního zpevnění je v korelaci s Guth-Gold rovnicí. Je předpokládáno, že nanočástice slouží jako další fyzikální zapleteniny a vedou k fyzikálně více zapletenému systému. Stejný efekt jako v elastické oblast tj. vliv velikosti částic na modul, byla pozorována i během deformačního zpevnění.
|
|
|
Structural-mechanical characteristics of the selected type of low-carbon steel after cold drawing and heat treatment
Stopka, Maroš ; Molliková, Eva (referee) ; Pacal, Bohumil (advisor)
This bachelor's thesis focuses on changes in the mechanical properties of low-carbon wire that has been cold-drawn and subsequently heat-treated. Mechanical tests, from which the values of elongation, yield strength and tensile strength were measured, were performed on all samples within 24 hours after they were collected. Two different production rates were established on the hot dip galvanizing line to achieve different time intervals of the annealing process. The experiment was performed at all stages of wire diameter reduction, including the input material. This work also includes metallographic analyzes of samples that have been both polished and etched. The most representative samples were selected for analysis. The results show that deformation caused changes in mechanical properties and an increase in strain hardening, which was subsequently removed by heat treatment.
|
|
|
Casting of manganese steels and their use
Dufka, Martin ; Šenberger, Jaroslav (referee) ; Pernica, Vítězslav (advisor)
Austenitic manganese steel, often referred as Hadfield´s steel after its discoverer, has an irreplaceable place in foundry due to its specific properties. Due to local pressures and shocks, surface of castings is hardened, but the cast core retains its toughness. Thus, manganese steel is used for castings of highly stressed machine parts that are subject to abrasive wear. This bachelor thesis is concerned about methods of production, chemical composition, influence of some alloying elements on properties and structure of steel, heat treatment, material properties, reinforcement mechanisms and types of individual deformation reinforcements. Further attention is paid to the most frequent use of manganese castings in practice.
|
|
|
DEFORMATION BEHAVIOR OF NANO/MICRO REINFORCED PMMA
Recman, Lukáš ; Nezbedová, Eva (referee) ; Kučera, Jaroslav (referee) ; Jančář, Josef (advisor)
Práce sleduje vliv velikosti částic na elastický modul a deformační chování za mezí kluzu. Bylo pozorováno, že jak elastická oblast, tak oblast za mezí kluzu ukazuje silnou závislost chování na velikosti částic. Cílem této práce je korelovat experimentální data a teoretické předpoklady které bylo odvozeny pro deformační chování v elastické oblasti a v oblasti za mezí kluzu pro amorfní polymery a konkrétně pro PMMA. Vše je motivováno propojit zatím oddělené oblasti kontinuální mikromechaniky a diskrétní nanomechaniky. Deformační chovaní PMMA plněného nano a mikro plnivem bylo pozorováno v elastické a plastické oblasti. Byl zkoumán vliv velikosti částic na velikost modulu a deformačního zpevnění. Mechanizmus vyztužení je interpretován s použitím teorie imobilizace řetězců, nanočástice mají silný vliv na molekulární dynamiku a kinetiku zapletenin. Mým příspěvkem k tomuto tématu je ukázat výraznou závislost na mechanizmu vyztužení v závislosti na velikosti částic. A to jak pod teplotou skelného přechodu tak nad teplotou skelného přechodu. Ačkoli pro velikost modulu byla publikována značná množství dat, která byla následně i interpretována, vliv částic na deformační zpevnění je poskrovnu. Během elastické deformace je primární struktura materiálu neměnná, jedná se o elastickou deformaci, za mezí kluzu již toto neplatí a primární struktura je zde nevratně poškozena. Bylo ukázáno, že obsah nano částic vede ke zvýšení meze kluzu a vyššímu deformačnímu zpevnění. Tento nárůst deformačního zpevnění je v korelaci s Guth-Gold rovnicí. Je předpokládáno, že nanočástice slouží jako další fyzikální zapleteniny a vedou k fyzikálně více zapletenému systému. Stejný efekt jako v elastické oblast tj. vliv velikosti částic na modul, byla pozorována i během deformačního zpevnění.
|