The Effect of Potassium Oxide K2O on the Purity of C3A
Jančíková, Andrea ; Ravaszová, Simona ; Dvořák, Karel ; Křištof, Michal
The article is devoted to the study of the preparation and stabilization of pure cubic phase of tricalcium aluminate C₃A. The findings from the literature and several experimental trials have been summarized. Based on these findings, the synthesis of C₃A was realized, and high purity of this mineral was achieved. Furthermore, the influence of foreign ions, mainly in the form of potassium oxide K₂O combined with Na₂O in the form of sodium oxide on the crystal structure was investigated. The transformation of the cubic phase of C₃A into an orthorhombic phase was observed when the amount of these ions in the structure was changed.
|
|
|
Calcium aluminate hydrates - laboratory preparation and characterisation
Koplík, Jan ; Opravil, Tomáš (referee) ; Šoukal, František (advisor)
Calcium aluminate phases are important parts of Ordinary Portland cement and Alumina cement. Various calcium aluminate hydrates originate during the hydration of calcium alumina phases. Their origin depends on the conditions of hydration. In the diploma thesis was investigated hydration of four calcium aluminate phases – CA, CA2, C12A7, C3A under the conditions of four pH – 6, 9, 11, 12,65. Calcium aluminate phases were prepared from CaCO3 and Al2O3 by clinkering in solid phase in laboratory oven. The phases were hydrated for 48 hours. Kinetics of the hydration was investigated by calorimetry. Calcium aluminate hydrates were identified by XRD and DTA.
|
|
|
Calcium aluminate hydrates - laboratory preparation and characterisation
Koplík, Jan ; Opravil, Tomáš (referee) ; Šoukal, František (advisor)
Calcium aluminate phases are important parts of Ordinary Portland cement and Alumina cement. Various calcium aluminate hydrates originate during the hydration of calcium alumina phases. Their origin depends on the conditions of hydration. In the diploma thesis was investigated hydration of four calcium aluminate phases – CA, CA2, C12A7, C3A under the conditions of four pH – 6, 9, 11, 12,65. Calcium aluminate phases were prepared from CaCO3 and Al2O3 by clinkering in solid phase in laboratory oven. The phases were hydrated for 48 hours. Kinetics of the hydration was investigated by calorimetry. Calcium aluminate hydrates were identified by XRD and DTA.
|