Properties of fibers based on polyhydroxybutyrate
Štulrajterová, Lujza ; Tocháček, Jiří (oponent) ; Přikryl, Radek (vedoucí práce)
This work deals with the melt spinning process of biopolymer fibers. Recent knowledge of poly(3-hydroxy butyrate) (PHB) and poly(lactic acid) (PLA) fiber spinning processes have been covered in the theoretical part. PHB based polymer blends of various composition were prepared to study the effect of PLA, different plasticizers and their content on the fiber properties. Three commercial plasticizers (ATBC, PEG, A6) and two experimentally synthesized were used. Spinning was carried out on three devices. Spinning on the conventional spinning lines with take-up speed exceeding 150 m/min was not accomplished. Lowe take-up speed was necessary due to insufficient melt strength. Fibers with drawing ratio of 6.4 were prepared and analyzed by GPC, MDSC and mechanical testing. According to the glass transition temperature results, ATBC and PEG have better plasticizing effect over the studied PLA/PHB blends than A6. Fibers containing A6 have the highest tensile strength and modulus of elasticity of 250 MPa and 2.7 GPa, respectively. At last, the effect of aging, thermal and hydrothermal treatment on mechanical properties of fibers was studied.
|
|
|
Změkčování poly(3-hydroxybutyrátu)
Brňák, Matúš ; Petruš, Josef (oponent) ; Kučera, František (vedoucí práce)
Bakalárska práca sa zaoberá zmäkčovaním PHB vybranými typmi zmäkčovadiel. Vplyv zmäkčovadiel je porovnávaný medzi sebou vzhľadom na ich vlastnosti a štruktúru. V teoretickej časti sú zhrnuté poznatky o zmäkčovaní polymérov a charakterizované jednotlivé druhy zmäkčovadiel. Experimentálna časť sa zaoberá samotným zmäkčovaním PHB v roztoku a tavenine. PHB bol rozpúšťaný v chloroforme a do vzniknutého roztoku boli pridávané zmäkčovadlá ATBC, TBC, ATEC, TEC, TOTM, PVAc a butylglykol s obsahom 30 hm %. Při zmäkčovaní v tavenine bola pripravená polymérna pasta s obsahom změkčovadla 70 hm % a 30 hm % PVAc. Zmes bola plastifikovaná v mixéri, pričom čas a želatinačná teplota boli stanovené experimentálne. Pomocou TGA boli stanovené hodnoty tepelnej degradácie pripravených vzoriek. DSC analýzou boli sledované hodnoty Tg, Tm a Xc. U vzoriek mäkčených v tavenine bola stanovená tvrdosť materiálu v stupnici Shore A a podľa Vickersa.
|
|
|
Properties of fibers based on polyhydroxybutyrate
Štulrajterová, Lujza ; Tocháček, Jiří (oponent) ; Přikryl, Radek (vedoucí práce)
This work deals with the melt spinning process of biopolymer fibers. Recent knowledge of poly(3-hydroxy butyrate) (PHB) and poly(lactic acid) (PLA) fiber spinning processes have been covered in the theoretical part. PHB based polymer blends of various composition were prepared to study the effect of PLA, different plasticizers and their content on the fiber properties. Three commercial plasticizers (ATBC, PEG, A6) and two experimentally synthesized were used. Spinning was carried out on three devices. Spinning on the conventional spinning lines with take-up speed exceeding 150 m/min was not accomplished. Lowe take-up speed was necessary due to insufficient melt strength. Fibers with drawing ratio of 6.4 were prepared and analyzed by GPC, MDSC and mechanical testing. According to the glass transition temperature results, ATBC and PEG have better plasticizing effect over the studied PLA/PHB blends than A6. Fibers containing A6 have the highest tensile strength and modulus of elasticity of 250 MPa and 2.7 GPa, respectively. At last, the effect of aging, thermal and hydrothermal treatment on mechanical properties of fibers was studied.
|
|
|
Změkčování poly(3-hydroxybutyrátu)
Brňák, Matúš ; Petruš, Josef (oponent) ; Kučera, František (vedoucí práce)
Bakalárska práca sa zaoberá zmäkčovaním PHB vybranými typmi zmäkčovadiel. Vplyv zmäkčovadiel je porovnávaný medzi sebou vzhľadom na ich vlastnosti a štruktúru. V teoretickej časti sú zhrnuté poznatky o zmäkčovaní polymérov a charakterizované jednotlivé druhy zmäkčovadiel. Experimentálna časť sa zaoberá samotným zmäkčovaním PHB v roztoku a tavenine. PHB bol rozpúšťaný v chloroforme a do vzniknutého roztoku boli pridávané zmäkčovadlá ATBC, TBC, ATEC, TEC, TOTM, PVAc a butylglykol s obsahom 30 hm %. Při zmäkčovaní v tavenine bola pripravená polymérna pasta s obsahom změkčovadla 70 hm % a 30 hm % PVAc. Zmes bola plastifikovaná v mixéri, pričom čas a želatinačná teplota boli stanovené experimentálne. Pomocou TGA boli stanovené hodnoty tepelnej degradácie pripravených vzoriek. DSC analýzou boli sledované hodnoty Tg, Tm a Xc. U vzoriek mäkčených v tavenine bola stanovená tvrdosť materiálu v stupnici Shore A a podľa Vickersa.
|