Fatigue life and fracture of cast gamma TiAl intermetallic alloy at room and elevated temperatures
 Petrenec, Martin ; Šmíd, Miroslav ; Polák, Jaroslav
The low-cycle fatigue properties, surface relief and fracture surfaces of cast TiAl alloys with 2 at.% Nb having nearly lamellar microstructure were studied at room temperature and at 750 degrees C. Cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures. The surface relief and the fracture surfaces of fractured specimens were observed using scanning electron microscopy. At room temperature, significant cyclic hardening is observed whereas at 750 degrees C cyclic response was stable. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. Persistent slip markings formed along interlamellar interfaces were predominant locations for fatigue cracks at both temperatures. The cracks initiated at surface or in sub-surface region led to the formation of smooth flat areas on the fracture surface corresponding to the persistent slip bands.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English