Modification of polymer blends based on polyhydroxybutyrate and their properties
Melčová, Veronika ; Tocháček, Jiří (oponent) ; Přikryl, Radek (vedoucí práce)
Theoretical part of this work describes properties and modification possibilities of poly(3-hydroxy butyrate) (PHB) and amorphous poly(lactic acid) (PLA) and their blends. In experimental part, reactivity of Joncryl, Raschig, and phosphite reagents triphenyl phosphite, tris(nonylphenyl) phosphite, and diphenyl isodecyl phosphite with neat PLA and PHB are studied. Raschig, an oligomeric polycarbodiimide based additive, was proven to enhance melt viscosity of both polymers in amount 2%wt., therefore was used for preparation of blends in five PHB/(PHB+PLA) ratios. Samples with Raschig and corresponding non-reactive samples were studied using rheology, gel permeation chromatography and modulated differential scanning calorimetry. Results showed possible reaction of Raschig and PHB/PLA blends leading to branched structures. However, the rate of reaction is not sufficient to completely compensate decrease in viscosity due to processing degradation. Thus, non-reacted amount of Raschig remains in matrix. On the basis of these findings, it is concluded that Raschig behaves rather as a relatively effective stabilizer of rheological properties than as a reagent for the intentional modification of PHB/PLA blends’ structure. In order to study mechanical properties of these blends, samples plasticized with acetyltributylcitrate were prepared using twin screw extruder.
|
|
|
Kompatibilizace směsí termoplastů s PLA
Petruš, Josef ; Petrůj, Jaroslav (oponent) ; Kučera, František (vedoucí práce)
Diplomová práce se zabývá přípravou polymerní směsi polymeru A s polymerem B. Dosavadní znalosti o vzniku a termodynamice polymerních směsí a úloze kompatibilizátoru podává teoretická část. Procesem fyzikální kompatibilizace byla připravena směs A/B o hmotnostních poměrech A/B 75/25, 50/50 a 25/75 hm %. Koncentrace použitého kompatibilizátoru byla 5 hm %, u směsi A/B 50/50 hm % 10 a 30 hm %. Proces mísení byl uskutečněn v dvoušnekovém extruderu při teplotě 230 °C a 100 rpm. Druhá metoda přípravy A/B směsí byla založena na in situ reaktivní kompatibilizaci, prováděné v mixéru Brabender při 230 °C a 50 rpm po dobu 10 minut. Hmotnostní obsah A a B byl opět 75/25, 50/50 a 25/75 hm %. Jako monomer byl zvolen anhydrid kyseliny itakonové (IAH) a maleinanhydrid (MAH) v koncentračním zastoupení 0,5 a 5 hm %, iniciátor reakce byl 2,5-dimethyl-2,5-bis(tert-buthylperoxy)hexan (Luperox 101). Rozdíl mezi kompatibilizovanými a nekompatibilizovanými směsmi byl charakterizován rastrovací elektronovou mikroskopií, tahovou zkouškou, diferenciální skenovací kalorimetrií, metodou stanovení indexu toku taveniny, acido-bazickou titrací a FT-IR spektroskopií.
|
|
|
Modification of polymer blends based on polyhydroxybutyrate and their properties
Melčová, Veronika ; Tocháček, Jiří (oponent) ; Přikryl, Radek (vedoucí práce)
Theoretical part of this work describes properties and modification possibilities of poly(3-hydroxy butyrate) (PHB) and amorphous poly(lactic acid) (PLA) and their blends. In experimental part, reactivity of Joncryl, Raschig, and phosphite reagents triphenyl phosphite, tris(nonylphenyl) phosphite, and diphenyl isodecyl phosphite with neat PLA and PHB are studied. Raschig, an oligomeric polycarbodiimide based additive, was proven to enhance melt viscosity of both polymers in amount 2%wt., therefore was used for preparation of blends in five PHB/(PHB+PLA) ratios. Samples with Raschig and corresponding non-reactive samples were studied using rheology, gel permeation chromatography and modulated differential scanning calorimetry. Results showed possible reaction of Raschig and PHB/PLA blends leading to branched structures. However, the rate of reaction is not sufficient to completely compensate decrease in viscosity due to processing degradation. Thus, non-reacted amount of Raschig remains in matrix. On the basis of these findings, it is concluded that Raschig behaves rather as a relatively effective stabilizer of rheological properties than as a reagent for the intentional modification of PHB/PLA blends’ structure. In order to study mechanical properties of these blends, samples plasticized with acetyltributylcitrate were prepared using twin screw extruder.
|
|
|
Kompatibilizace směsí termoplastů s PLA
Petruš, Josef ; Petrůj, Jaroslav (oponent) ; Kučera, František (vedoucí práce)
Diplomová práce se zabývá přípravou polymerní směsi polymeru A s polymerem B. Dosavadní znalosti o vzniku a termodynamice polymerních směsí a úloze kompatibilizátoru podává teoretická část. Procesem fyzikální kompatibilizace byla připravena směs A/B o hmotnostních poměrech A/B 75/25, 50/50 a 25/75 hm %. Koncentrace použitého kompatibilizátoru byla 5 hm %, u směsi A/B 50/50 hm % 10 a 30 hm %. Proces mísení byl uskutečněn v dvoušnekovém extruderu při teplotě 230 °C a 100 rpm. Druhá metoda přípravy A/B směsí byla založena na in situ reaktivní kompatibilizaci, prováděné v mixéru Brabender při 230 °C a 50 rpm po dobu 10 minut. Hmotnostní obsah A a B byl opět 75/25, 50/50 a 25/75 hm %. Jako monomer byl zvolen anhydrid kyseliny itakonové (IAH) a maleinanhydrid (MAH) v koncentračním zastoupení 0,5 a 5 hm %, iniciátor reakce byl 2,5-dimethyl-2,5-bis(tert-buthylperoxy)hexan (Luperox 101). Rozdíl mezi kompatibilizovanými a nekompatibilizovanými směsmi byl charakterizován rastrovací elektronovou mikroskopií, tahovou zkouškou, diferenciální skenovací kalorimetrií, metodou stanovení indexu toku taveniny, acido-bazickou titrací a FT-IR spektroskopií.
|
|
| |
|
| |
|
| |