ASSESSMENT OF REINFORCED CONCRETE STRUCTURES EXPOSED TO ELEVATED TEMPERATURES
Rozsypalová, Iva ; Kolář,, Karel (referee) ; Vítek,, Jan (referee) ; Daněk, Petr (advisor)
Doctoral thesis is focused on the assessment of concrete structures after fire exposure and extends the knowledge in view of the main aims of the research defined in the objectives of his work. Thanks to the performed fire tests of full-scale concrete specimens, material characteristics corresponding to actual fire load have been assessed for different temperature levels. Resulting from presented research, main steps of assessment procedure have been recommended for both destructive and non-destructive tests of concrete after exposure to fire. Furthermore, behaviour of FRP reinforcement at elevated temperatures have been investigated. Aiming to determine the effects of fire exposure on reinforced concrete structures, experimental program have been defined and performed, including concrete beams reinforced with either steel, or composite reinforcement with glass or carbon fibres and subjected to experimentally simulated fire load. After cooling, bending test have been executed. Above mentioned experimental program was further complemented by extensive numerical analysis. Finally, presented work provides guidelines regarding further investigations required in this field of research.
|
|
|
Complex diagnostics static structural condition of the building
Voltr, Vojtěch ; Rozsypalová, Iva (referee) ; Schmid, Pavel (advisor)
This diploma thesis deals with the problems of revitalization of historical objects. The theoretical part describes the technologies for static reinforcing and rehabilitation of vertical and horizontal bearing structures for a purpose of increasing the general stiffness of the object. As the practical part a static design project is made for reinforcing of the bearing walls and also for the general reconstruction of the slab. The slab is designed as the composite timber-concrete structure. The design project of the slab is economically compared with other variants. The designs are made for an existing object of the old restaurant in the village Velichovky.
|
|
|
Comparison of selected parameters of tensile strength of concrete
Rozsypalová, Iva ; Žítt, Petr (referee) ; Daněk, Petr (advisor)
The thesis deals with a comparison of the selected strength tension properties of the hardened concrete and finding relationships between them. This is essentially a simple tensile strength, tensile flexural strength and tensile splitting strength. The text describe the testing procedures to determine the tensile strength of concrete. Furthermore, there are presented the results of testing on different types of concrete (plain concrete, lightweight concrete, steel-fiber concrete, polymer-fibre concrete and high strength concrete). The conclusion deals with the derivation of dependancy between concrete strengths and comparing the values obtained from the available relations with the results of the tests.
|
|
| |
|
| |
|
|
ASSESSMENT OF REINFORCED CONCRETE STRUCTURES EXPOSED TO ELEVATED TEMPERATURES
Rozsypalová, Iva ; Kolář,, Karel (referee) ; Vítek,, Jan (referee) ; Daněk, Petr (advisor)
Doctoral thesis is focused on the assessment of concrete structures after fire exposure and extends the knowledge in view of the main aims of the research defined in the objectives of his work. Thanks to the performed fire tests of full-scale concrete specimens, material characteristics corresponding to actual fire load have been assessed for different temperature levels. Resulting from presented research, main steps of assessment procedure have been recommended for both destructive and non-destructive tests of concrete after exposure to fire. Furthermore, behaviour of FRP reinforcement at elevated temperatures have been investigated. Aiming to determine the effects of fire exposure on reinforced concrete structures, experimental program have been defined and performed, including concrete beams reinforced with either steel, or composite reinforcement with glass or carbon fibres and subjected to experimentally simulated fire load. After cooling, bending test have been executed. Above mentioned experimental program was further complemented by extensive numerical analysis. Finally, presented work provides guidelines regarding further investigations required in this field of research.
|
|
|
Characterization of Božanov sandstone: pilot fracture tests
Kumpová, I. ; Rozsypalová, I. ; Vavro, Leona ; Vavro, Martin ; Keršner, Z.
The aim of this paper is a characterization ofsandstone from Božanov quarry near Broumov, Czech Republic,by means of the pilot fracture tests. Five drill-core test specimens withnominal diameter of 50mm and lengths of 100 and 125mmwere provided by an initial chevron type notch. Specimens were loaded in the configuration of the three-point bending as a displacement driven experimentusing LabTest 6.250 equipment in the laboratory of the Institute of Building Testing, Faculty of Civil Engineering, Brno University of Technology. The load versus displacement diagrams were used to quantify the basic mechanical fracture parameters of the studied sandstone: modulus of elasticity, fracture toughness, toughness, and specific fracture energy.
|
|
|
X-ray micro-tomography characterization of voids caused by three-point bending in selected alkali-activated aluminosilicate composite
Kumpová, Ivana ; Rozsypalová, I. ; Keršner, Z. ; Rovnaníková, P. ; Vopálenský, Michal
This paper deals with the pilot characterization of a special alkali-activated aluminosilicate composite composed of waste brick powder, brick rubble and a solution of potassium water glass. Fracture tests were conducted on the specimens via three-point bending and fracture parameters were evaluated. Selected specimen was investigated using micro-tomography to supplement the results with visual information about the inner structure of this newly designed material before and after the mechanical loading. Tomographic measurements and image processing were conducted for a qualitative and quantitative assessment of changes in the internal structure with an emphasis on the calculation of porosimetric parameters and visualization of the fracture surface. Fractal dimension of fracture surface was estimated.
|
|
|
Fracture Parameters of AAAS composites with ceramic precursor
Šimonová, H. ; Rozsypalová, I. ; Kumpová, Ivana ; Trčka, T. ; Frantík, P. ; Rovnaníková, P. ; Keršner, Z.
The paper deals with alkali-activated aluminosilicate composites based on ceramic precursors with respect to their characterization by fracture-mechanical parameters. Three composites made of brick dust as a precursor and alkaline activator with silicate modulus Ms = 1.0, 1.2 and 1.4 were investigated. After 28 days of maturation, specimens with nominal dimensions of 40 × 40 × 160 mm were provided by an initial notch to 1/3 of the body height in the middle of the span. At least 6 samples were tested from each composite. Specimens were subjected to three-point bending tests during which force vs. deflection at midspan (F–d) and force vs. crack mouth opening displacement (F–CMOD) diagrams were recorded. By processing these diagrams, the values of the static modulus of elasticity, the effective fracture toughness (including its initiating component) and the specific fracture energy were determined using the effective crack model, Work-of-Fracture method, and Double-K fracture model. After the fracture experiments had been performed, compressive strength values were determined for informational purposes from one part of each specimen that remained after testing. All evaluations included the determination of arithmetic means and standard deviations. To obtain information about the internal structure of composites before and after mechanical testing, the selected body was examined by micro-tomography. Tomographic measurements and image processing were performed for qualitative and quantitative evaluation of internal structure changes with an emphasis on the calculation of porosimetric parameters as well as visualization of the fracture process zone. The fractal dimension of fracture objects was determined.
|
|
|
Possibilities of using 4D computed tomography in fracture tests
Kumpová, Ivana ; Fíla, Tomáš ; Koudelka, Petr ; Rozsypalová, I. ; Keršner, Z. ; Kytýř, Daniel ; Vopálenský, Michal ; Vavřík, Daniel ; Vyhlídal, M. ; Drdácký, Miloš
The paper presents the study of the internal structure and fracture properties of selected quasi-brittle building materials subjected to temperature changes and the possibility of applying the method combining bending fracture tests and time-dependent computed tomography (4D CT). The tested specimens were subjected to hightemperature effects and subsequently tested by a four-point bending during 4D CT. Thus, 3D image information was obtained in different phases of loading and material damage. Comparative compression strength measurements were also performed. These results are in good agreement
|