Fatigue-creep interaction in Ni superalloys and TiAl alloys
 Šmíd, Miroslav ; Věchet, Stanislav (referee) ; Kunz, Ludvík (referee) ; Obrtlík, Karel (advisor)
The present doctoral thesis is focused on the effect of dwells on the low cycle fatigue behaviour of advanced high temperature materials. 10 minutes strain holds are introduced into the cyclic straining of cast Ni-based superalloy IN792-5A and cast intermetallic alloy TiAl-7Nb which were chosen as experimental material. Fatigue experiments were conducted in strain control mode with constant total strain amplitude and strain rate. IN792-5A was subjected to continuous cyclic loading test as well as fatigue tests either with tensile peak strain holds or compressive peak strain holds at temperature 800 °C. TiAl-7Nb was experimentally examined by continuous cyclic loading tests and also by fatigue test with tensile peak strain hold times at temperature 750 °C. Cyclic hardening/softening curves, cyclic stress-strain curves, Manson-Coffin curves and Basquin curves were obtained. Stress relaxation data were measured during hold times. Mean stress evolution was observed and documented. Microstructure of both alloys was observed in as-received state and also after cyclic loading by means of SEM and TEM. Surface relief investigation revealed cyclic plastic strain localisation as well as fatigue crack initiation sites. Fatigue crack propagation was described using fracture surface and longitudinal gauge section observations. Dislocation structures developed in the course of fatigue tests were studied and documented.
Detailed record
Fatigue-creep interaction in Ni superalloys and TiAl alloys
 Šmíd, Miroslav ; Věchet, Stanislav (referee) ; Kunz, Ludvík (referee) ; Obrtlík, Karel (advisor)
The present doctoral thesis is focused on the effect of dwells on the low cycle fatigue behaviour of advanced high temperature materials. 10 minutes strain holds are introduced into the cyclic straining of cast Ni-based superalloy IN792-5A and cast intermetallic alloy TiAl-7Nb which were chosen as experimental material. Fatigue experiments were conducted in strain control mode with constant total strain amplitude and strain rate. IN792-5A was subjected to continuous cyclic loading test as well as fatigue tests either with tensile peak strain holds or compressive peak strain holds at temperature 800 °C. TiAl-7Nb was experimentally examined by continuous cyclic loading tests and also by fatigue test with tensile peak strain hold times at temperature 750 °C. Cyclic hardening/softening curves, cyclic stress-strain curves, Manson-Coffin curves and Basquin curves were obtained. Stress relaxation data were measured during hold times. Mean stress evolution was observed and documented. Microstructure of both alloys was observed in as-received state and also after cyclic loading by means of SEM and TEM. Surface relief investigation revealed cyclic plastic strain localisation as well as fatigue crack initiation sites. Fatigue crack propagation was described using fracture surface and longitudinal gauge section observations. Dislocation structures developed in the course of fatigue tests were studied and documented.
Detailed record

Interested in being notified about new results for this query?
Subscribe to the RSS feed.
Digital Repository :: Search :: Submit :: Personalize :: Help
Powered by Invenio v1.1.2
Maintained by admin.invenio@techlib.cz
This site is also available in the following languages:
Česky  English