Verification of computer simulation in the field of thermal properties of foundry moulds
Šupa, Jan ; Rusín, Karel (referee) ; Cupák, Petr (advisor)
This diploma thesis deals with thermal qualities of moulding mixtures of foundry mould of various types of sand grains and a computer simulation of the solidification of the cast. The aim of this work is to compare the values of thermal qualities of moulding materials bonded with water glass taken in experimental measurements to the values of thermal qualities of moulding materials connected with organic binding agent contained in simulation software. A sample cast will be moulded in order to evaluate cooling capacities of individual moulding mixtures according the shift of thermal axis. These results will consequently be compared to the results of the simulation.
|
|
|
Binder systems on the base aluminasilicate
Tůmová, Veronika ; Cupák, Petr (referee) ; Rusín, Karel (advisor)
This thesis describes influence of plasticizers and setting accelerators in binder system based aluminasilikates. Following survey includes changes of characteristics of aluminate cements in combination with various setting accelerators. Practical testing and measuring summarizes and compares interdependence of structure, compressive strength, permeability and abrasion resistance. As a final part of thesis individual mixes are analysed economically and are accompanied by suggestions for future use and use in working experience.
|
|
|
Water soluble foundry binders with heat dehydratation hardening
Šebesta, Pavel ; Rusín, Karel (referee) ; Cupák, Petr (advisor)
Environmental pressure on foundries has forced manufacturers to develop new organic and inorganic binders. One of the options is water soluble binders that can be hardened by dehydration. In addition to tenacity characteristics and regenerability of the forming mixtures another considered aspect is the amount of emissions generated by casting. Use of these new binders does not require expensive modifications of the machines for work with the forming mixtures.
|
|
| |
|
| |
|
|
Water soluble foundry binders with heat hardening
Vaverka, Jiří ; Rusín, Karel (referee) ; Cupák, Petr (advisor)
This thesis is focused on water soluble foundry binders with heat hardening. The thesis comprises general description of moulding mixtures, the description of the most common methods used for heat hardening and primarily the list of current and alternative binders, which reduce negative environmental impact of foundries. Also their qualities, benefits and drawbacks are included.
|
|
|
Influence of type of base sand on strength of geopolymer sand mixture
Kudr, Martin ; Šupálek, Milan (referee) ; Cupák, Petr (advisor)
The goal of this research is to find out the effect of different types of opening material on bending strength geopolymer’s moulding mixture. Four different silical opening material were used along with two types of binder. To solve the selected problem I have used the test of bending strength. At first I have prepared the moulding mixture and after its induration, I have tested the bending strength. The times were always the same 60, 120 and 1440 minutes. The highest level of bending strength was achieved at opening material SH-34 when using binder Geopol 618. The value of bending strength level was 0,881MPa. The results of this research could help the foundries during implementing technology of geopolymer moulding mixture, which would help particulary when looking for a proper opening material.
|
|
| |
|
| |
|
|
Systems of self-setting foundry mixtures on the base portland cements
Janíčková, Petra ; Cupák, Petr (referee) ; Rusín, Karel (advisor)
The project elaborated in frame of engineering studies branch N2332-00. The project is submitting design of technology production sand mixture with cement binder – Portland binder CEM I 42,5 N. Pursuant to of the literary pursuit a problem of the sand mixture with cement binder was tested few sand mixture. As optimal composition it turned out application sand mixture with 2 % CaCl2 content and 1 – 2 % Dextrin content. Sand mixture with cement has good moulder and regenerating.
|