Short fatigue crack propagation description
Trávníček, Lukáš ; Náhlík, Luboš (referee) ; Hutař, Pavel (advisor)
The presented master’s thesis deals with description of short fatigue cracks and can be divided to the several parts. In the first part, theoretical background of fatigue of materials and fracture mechanics parameters which can describe fatigue cracks is presented. Following part describes how to determine fracture mechanics parameters by finite elements method. Due to the shape of propagated fatigue crack, numerical model was established as a three-dimensional. Results obtained based on this model, was compared with literature with very good agreement. Than real shape of propagated short crack was used for description of the experimental data. It was shown, that plastic part of J-integral is suitable parameter for description of the short cracks.
|
|
|
Short fatigue crack propagation description
Trávníček, Lukáš ; Náhlík, Luboš (referee) ; Hutař, Pavel (advisor)
The presented master’s thesis deals with description of short fatigue cracks and can be divided to the several parts. In the first part, theoretical background of fatigue of materials and fracture mechanics parameters which can describe fatigue cracks is presented. Following part describes how to determine fracture mechanics parameters by finite elements method. Due to the shape of propagated fatigue crack, numerical model was established as a three-dimensional. Results obtained based on this model, was compared with literature with very good agreement. Than real shape of propagated short crack was used for description of the experimental data. It was shown, that plastic part of J-integral is suitable parameter for description of the short cracks.
|
|
|
Růst krátkých trhlin ve feriticko-perliticko-bainitické oceli
Polák, Jaroslav
The initiation and the growth of short cracks were studied in ferritic-pearlitic-bainitic steel. Short cracks initiate preferably in persistent slip markings in areas of proeutectoid ferrite. The kinetics of short crack growth is characterized by exponential growth. Crack growth coefficient was found to be a function of plastic strain amplitude. The comparison of the short crack growth kinetics with Coffin-Manson law allows determining the parameters of the short crack growth law from the low cycle fatigue experiments
|
|
|
Růst krátkých trhlin z vrubů ve dvoufázové austenitcko-feritické oceli
Kotecký, Ondřej ; Degallaix, S. ; Polák, Jaroslav
The effect of microstructure and stress gradient in a two-phase austenitic-ferritic steel in specimens with confined plasticity is studied. Direct optical observations and potential drop technique calibrated via the finite element method are used to measure the surface crack size and its depth and to determine the surface crack growth. The effect of stress and strain gradients on the crack propagation kinetics and crack shape is evaluated and dicussed.
|
|
| |