Study of the properties of fillers to the composites requiring high temperature resistance
Vovesný, Václav ; Gross,, Tomáš (referee) ; Bydžovský, Jiří (advisor)
The diploma thesis is focused on the behaviour of natural and synthetic aggregates and their behaviour in polymer – cement composites, while being exposed to high temperature. The processes, happening in aggregates and mortar under the thermal load, were described in the theoretical part of the thesis same as the testing of heat effects on the aggregates and mortar. Further, the influence of high temperature on each component of concrete was described, followed by the suggestion of the appropriate components for concrete exposed to high temperature. Various aggregates were tested in the experimental part of the thesis. The basic physical and mechanical properties of aggregates were examined same as their mineralogical composition with using XRD, DTA and SEM methods. At the mortar, the influence of high temperature on the concrete density, compressive strength and tensile strength was defined. The gained knowledge was evaluated in the final part of the thesis
|
|
|
Development of Resistant Coating Systems Based on Polymer Binders
Voráčová, Veronika ; Vyhnánek, Miroslav (referee) ; Petránek, Vít (advisor)
The aim of the thesis is to propose the use of waste materials as filler for the selected coating systems used for chemical protection of concrete surfaces.The used filler could not affect the existing binder of the coating system. Research was conducted using two materials N141 and N 121. The waste material was chosen by his chemical and physical properties. Between suitable materials belongs slag, fly ash, foundry sand and glass waste. The selection based on Lena Chemical s.r.o companies request was selected glass waste. The practical part includes examination as fillers, and the corresponding tests for coating systems with pre-used filler. Finally, the assessment of the suitability of the materials used.
|
|
|
Evaluation of local filler sources suitability for anhydrite-based screeds
Šikral, Martin ; Kaláb, Michal (referee) ; Drochytka, Rostislav (advisor)
Goal of this thesis is to evaluate suitability of local filler sources for anhydrite based screed floor covers. The theoretical part is mostly aimed at summarization of general findings about flooring constructions and about anhydrite itself. The thesis also includes description of primary and secondary raw materials. The goal of this work is to suggest suitable fillers for anhydrite based screed floor covers in accordance with distance from Sika CZ, s.r.o with residence in Brno – Modrice. At the same time this thesis explores possibility of secondary raw materials usage as a replacement of primary fillers. In conclusion the thesis focuses on the laboratory test of chosen fillers, summarization and discussion of discovered findings.
|
|
|
Inorganic fillers effect on electrical properties of the epoxy resins
Doležel, Tomáš ; Jirák, Josef (referee) ; Frk, Martin (advisor)
This thesis deals with problems of electrical insulation materials based on epoxy composites used in the electronics industry. This thesis is divided into theoretical part focused on composite materials, their technological processing and diagnostics. It also describes dielectric materials, their properties and events taking place in their structure. The experimental section describes the measurement of electrical properties of samples of electrical insulating materials with different types of fillers.
|
|
|
Photopolymerization kinetics of dimethacrylate dental resin
Vaněk, Martin ; Bystřický, Zdeněk (referee) ; Poláček, Petr (advisor)
Aim of magister´s thesis was to study reaction kinetics of dental materials. Thesis was focused on dimethacrylate dental polymers, which are for example used for dental restoration, tooth repair and creating now teeth. First part of the thesis concentrates on influence of molar ratio on reation kinetics by addition of other monomer to polymer resin. Second part concentrates on influence of addition of additive silica on reaction kinetics of polymerization. Essential variables know as a polymerization ratio, conversion, gel point, glass transition temperature and storage modulus were studied. Firstly, polymerization ratio and conversion were observed by differential scanning calorimetry (DSC). Secondly rheology was observed by photoreometr. Finally, glass transition temperature and storage modulus were observed by dynamic mechanical analysis (DMA). Behaviour changes caused by addion of monomer or filler point out decrease of polymeration ratio and converstion. Same behaviour was observed by short exposure. In order to established network formation, values of gel point increased by higher concentration of monomer or filler. Glass transition temperature and storage modulus measured by DMA were evaluated. Those valuables had variable tendency due to monomer acting like filler at higher concentration. Also contradictory impact of different material conversion and filler concetration was discussed.
|
|
|
Interaction between asphalt binder and filler
Indráková, Kristýna ; Hýzl, Petr (referee) ; Dašek, Ondřej (advisor)
The thesis is mainly focused on comparison of properties of mastics, that were mixed in lab. The samples of mastics were mixed of paving bitumen in combination with 9 samples of backhouse filler, 1 inappropriate sample containing mica and 1 sample of additive filler. The folowing tests were used for assessment of samples: The particle density of filler-pyknometer method, The delta ring and ball test, The complex shear modulus and phase angle, The multiple stress creep and recovery test. The tests results were evaluated and compared. The results of the thesis are listed in the conclusion.
|
|
|
Technological stage of Siding of a Block of Flats
Kasza, Radomír ; Ing.Lukáš Kopecký (referee) ; Diaz, Yvetta (advisor)
Bachelor thesis solves the construction and assembly phase of the technological envelope of a residential building in the Český Těšín. Includes integrated parts for the implementation of this phase. Includes the plan of tests and controls, technological standard, plan of the risks, financial plan and timetable. In addition, an inventory of machines and principles of organization development.
|
|
|
Analysis of filler types onto the wood plastics composites
Blaha, Lukáš ; Pospíšil,, Ladislav (referee) ; Vaněrek, Jan (advisor)
Wood polymer composite (WPC) is a material that combines the wood material and the thermoplastic matrix. As filler to be used as wood flour and thermoplastic matrix will be used in primary or recycled polypropylene. WPC will be made by injection molding. The aim of the thesis is to find the optimal ratio between primary and recycled polymer in which the result will be the best physical and mechanical properties.
|
|
|
Design of vapor proof protective coating for concrete with chemical resistance
Fousková, Marika ; Hodná, Jana (referee) ; Drochytka, Rostislav (advisor)
The main content of the bachelor's thesis is to design a vapor-tight chemically resistant coating using secondary raw materials. Coatings are applied primarily for the purpose of protecting concrete structures that are exposed to chemical stress. Secondary raw materials are used in the coating in the form of a microfiller, which is evenly dispersed in the polymer matrix. The proposed coatings show high adhesion to concrete, excellent workability and applicability, while the filler in the form of secondary raw materials does not impair the properties of the coating, both in fresh and polymerized state.
|
|
|
Development of a thermal insulating material designed for use with high temperature
Dokoupil, Martin ; Frajt, Daniel (referee) ; Drochytka, Rostislav (advisor)
The work deals with the development of a new thermal insulation material that contains a secondary raw materials or waste. It is an insulating material with the requirement of resistance to high temperatures - 200 ° C and 500 ° C. Type of material is determined by the way of reducing density - direct and indirect. Direct is achieved by adding lightweight aggregates, indirect is achieved by gas evolution through chemical reaction and the subsequent incorporation of gas into the structure of the material. This thesis is part of the MPO TIP č. FR-TI 2/340 project.
|