Porušování jemnozrnného cementového kompozitu v blízkosti rozhraní plniva a matrice
Vyhlídal, Michal ; Kabele,, Petr (referee) ; Profant, Tomáš (referee) ; Keršner, Zbyněk (advisor)
The Interfacial Transition Zone (ITZ) between the aggregate grain/reinforcement bar and the matrix is considered to be the weakest element in cementitious composites and is, according to some authors, directly responsible for the nonlinear (more precisely, quasi-brittle) behavior of the composites. The aim of this work is verification of the generally accepted paradigm of the weakest element by means of fracture experiments and corresponding numerical simulations. In the experimental part, in addition to traditional fracture tests, modern methods of 3D scanning, scanning electron microscopy, chemical analysis using an electron microprobe and nanoindentation were used. In the numerical part, models based on generalized linear elastic fracture mechanics as well as modern models intended for the simulation of cement composites, namely crack band model with smeared cracks and the Microplane model, were used. Based on the results, the numerical part was complemented by the Cohesive Zone Material model simulating the behavior of the interface. All results are discussed and put into context with already published work. The main conclusion of the work is that the properties of the ITZ do not have such an influence on the behavior of cement composites as the adhesion between the inclusion and the ITZ, i.e. the matrix.
|
|
|
Study of plasmachemical reduction of corrosive layers on brass
Řádková, Lucie ; Selucká, Alena (referee) ; Krčma, František (advisor)
The main topic of this bachelor thesis is plasmachemical treatment of archeological artifacts, especially plasma chemical treatment of brass corrosion layers. Low-pressure, low-temperature hydrogen plasma is used for this process. Nowadays, the technology is used mainly for iron or silver based materials but even for them the optimal conditions for the corrosion removal are not fully known yet. The knowledge about other metallic materials is fully missing. Two sets of brass samples were prepared in different corrosion atmospheres. The first atmosphere was prepared using saturated vapors of HCl. The samples were in this atmosphere during one month, and corrosion layers were orange-brown. The second set was prepared using ammonium solution, the samples were in this atmosphere for one day, corrosion layers were blue. The generation of capacitively coupled plasma in continuous mode by different supplied power was done. The experiments were carried out at 100 Pa with hydrogen gas flow of 50 sccm. Discharge power was varied in the interval 50 – 200 W and the treatment duration was 70 – 140 min. The optical emission spectroscopy of OH radical was used to find out all changes those have been resulting from plasmachemical reactions. The OH radical integral intensities were observed, they were used to monitoring plasma chemical reduction process. Spectral intensity of spectroscope was in the range 290 – 330 nm. After the plasmachemical treatment, it was very difficult to remove corrosion layers of HCl, but removing of NH3 corrosion layers was easy. It was caused by type of corrosion process (corrosion layers were influenced by time of corrosion process). This bachelor thesis is the start to find out conduct corrosion layers of brass in plasma treatment. In future, plasma treatment could be used to treatment of real archaeological artifacts.
|
|
|
Reduction of bronze corrosion layers using hydrogen plasma
Miková, Petra ; Selucká, Alena (referee) ; Krčma, František (advisor)
This diploma thesis is focused to the plasma chemical reduction of model corrosion layers prepared on bronze samples. Bronze was the main material for production of the subjects in Bronze Age. First, it was very rare, and therefore was used only for making jewellery and other decorative subjects. Later, the objects of daily use and weapons were produced of bronze. These objects are found and it is necessary to restore him and preserve the cultural heritage for future generations. The research and the optimalization of plasmochemical reduction of model corrosion layers on bronze samples contributes to this. A metallographic grinder was used to create a defined surface, first with the sandpaper P 280 and then after sample 90 degree rotation with the sandpaper P 600. This ensured uniform surface at all bronze samples that is necessary to provide the same corrosion conditions. The grinded samples were washed by ethanol and dried by hot air stream. To prevent contact with the surrounding atmosphere and successive initiation of corrosion, the samples were stored in lockable polyethylene bags. This step was followed by the preparation of model corrosion layers. Hydrochloric and sulfuric acids were chosen as corrosive environments. Petri dish containing 20 ml of the selected acid was placed at the bottom of the desiccator. Samples were placed to the ceramic grate, over the dish, and they were corroded (in vapours of hydrochloric acid for 34 days and in vapours of sulfuric acid for 27 days). The corroded samples were treated using low-pressure hydrogen plasma excited by RF generator. Treatment of samples was carried out in quartz cylindrical reactor (length of 90 cm, inner diameter 9.5 cm) with copper electrodes placed outside. The pressure in the reactor was ranged around 160 Pa at hydrogen flow rate of 50 sccm during the experiments. The continuous and pulse modes (duty cycle of 25%, 50% or 75%) at peak power of 50–300 watts were used for the treatment of 90 minutes duration. The plasma treatment was monitored by optical emission spectroscopy of OH radical using compact Ocean Optics HR4000 spectrometer. Its integral intensity is proportional to the corrosion layer removal. The rotational temperatures of plasma were calculated using selected OH rotational lines, too. The sample temperature during the treatment was measured by thermocouple installed inside the additional non-corroded samples. The reduction of corrosion layer is successful when the maximum of relative intensity of OH radicals is produced and follow gradual decline. The samples which corroded in vapours of sulphuric acid and were treated in pulse modes with duty cycle of 25 % or with delivered power of 50 W has produced no maximum. To the remain samples the maximum although were observed, but reduced corrosion products on the surface were very cohesive. The maximum of relative intensity of OH radicals was observed at all samples corroded in vapours of hydrochloric acid. But there is problem with temperature of sample during experiment. The samples which layer of corrosion product was after experiment incoherent produced the layer of deposit tin. This effect formation at a higher temperature of sample during experiment and therefore with greater deliver energy.
|
|
|
Porušování jemnozrnného cementového kompozitu v blízkosti rozhraní plniva a matrice
Vyhlídal, Michal ; Kabele,, Petr (referee) ; Profant, Tomáš (referee) ; Keršner, Zbyněk (advisor)
The Interfacial Transition Zone (ITZ) between the aggregate grain/reinforcement bar and the matrix is considered to be the weakest element in cementitious composites and is, according to some authors, directly responsible for the nonlinear (more precisely, quasi-brittle) behavior of the composites. The aim of this work is verification of the generally accepted paradigm of the weakest element by means of fracture experiments and corresponding numerical simulations. In the experimental part, in addition to traditional fracture tests, modern methods of 3D scanning, scanning electron microscopy, chemical analysis using an electron microprobe and nanoindentation were used. In the numerical part, models based on generalized linear elastic fracture mechanics as well as modern models intended for the simulation of cement composites, namely crack band model with smeared cracks and the Microplane model, were used. Based on the results, the numerical part was complemented by the Cohesive Zone Material model simulating the behavior of the interface. All results are discussed and put into context with already published work. The main conclusion of the work is that the properties of the ITZ do not have such an influence on the behavior of cement composites as the adhesion between the inclusion and the ITZ, i.e. the matrix.
|
|
|
Reduction of bronze corrosion layers using hydrogen plasma
Miková, Petra ; Selucká, Alena (referee) ; Krčma, František (advisor)
This diploma thesis is focused to the plasma chemical reduction of model corrosion layers prepared on bronze samples. Bronze was the main material for production of the subjects in Bronze Age. First, it was very rare, and therefore was used only for making jewellery and other decorative subjects. Later, the objects of daily use and weapons were produced of bronze. These objects are found and it is necessary to restore him and preserve the cultural heritage for future generations. The research and the optimalization of plasmochemical reduction of model corrosion layers on bronze samples contributes to this. A metallographic grinder was used to create a defined surface, first with the sandpaper P 280 and then after sample 90 degree rotation with the sandpaper P 600. This ensured uniform surface at all bronze samples that is necessary to provide the same corrosion conditions. The grinded samples were washed by ethanol and dried by hot air stream. To prevent contact with the surrounding atmosphere and successive initiation of corrosion, the samples were stored in lockable polyethylene bags. This step was followed by the preparation of model corrosion layers. Hydrochloric and sulfuric acids were chosen as corrosive environments. Petri dish containing 20 ml of the selected acid was placed at the bottom of the desiccator. Samples were placed to the ceramic grate, over the dish, and they were corroded (in vapours of hydrochloric acid for 34 days and in vapours of sulfuric acid for 27 days). The corroded samples were treated using low-pressure hydrogen plasma excited by RF generator. Treatment of samples was carried out in quartz cylindrical reactor (length of 90 cm, inner diameter 9.5 cm) with copper electrodes placed outside. The pressure in the reactor was ranged around 160 Pa at hydrogen flow rate of 50 sccm during the experiments. The continuous and pulse modes (duty cycle of 25%, 50% or 75%) at peak power of 50–300 watts were used for the treatment of 90 minutes duration. The plasma treatment was monitored by optical emission spectroscopy of OH radical using compact Ocean Optics HR4000 spectrometer. Its integral intensity is proportional to the corrosion layer removal. The rotational temperatures of plasma were calculated using selected OH rotational lines, too. The sample temperature during the treatment was measured by thermocouple installed inside the additional non-corroded samples. The reduction of corrosion layer is successful when the maximum of relative intensity of OH radicals is produced and follow gradual decline. The samples which corroded in vapours of sulphuric acid and were treated in pulse modes with duty cycle of 25 % or with delivered power of 50 W has produced no maximum. To the remain samples the maximum although were observed, but reduced corrosion products on the surface were very cohesive. The maximum of relative intensity of OH radicals was observed at all samples corroded in vapours of hydrochloric acid. But there is problem with temperature of sample during experiment. The samples which layer of corrosion product was after experiment incoherent produced the layer of deposit tin. This effect formation at a higher temperature of sample during experiment and therefore with greater deliver energy.
|
|
|
Study of plasmachemical reduction of corrosive layers on brass
Řádková, Lucie ; Selucká, Alena (referee) ; Krčma, František (advisor)
The main topic of this bachelor thesis is plasmachemical treatment of archeological artifacts, especially plasma chemical treatment of brass corrosion layers. Low-pressure, low-temperature hydrogen plasma is used for this process. Nowadays, the technology is used mainly for iron or silver based materials but even for them the optimal conditions for the corrosion removal are not fully known yet. The knowledge about other metallic materials is fully missing. Two sets of brass samples were prepared in different corrosion atmospheres. The first atmosphere was prepared using saturated vapors of HCl. The samples were in this atmosphere during one month, and corrosion layers were orange-brown. The second set was prepared using ammonium solution, the samples were in this atmosphere for one day, corrosion layers were blue. The generation of capacitively coupled plasma in continuous mode by different supplied power was done. The experiments were carried out at 100 Pa with hydrogen gas flow of 50 sccm. Discharge power was varied in the interval 50 – 200 W and the treatment duration was 70 – 140 min. The optical emission spectroscopy of OH radical was used to find out all changes those have been resulting from plasmachemical reactions. The OH radical integral intensities were observed, they were used to monitoring plasma chemical reduction process. Spectral intensity of spectroscope was in the range 290 – 330 nm. After the plasmachemical treatment, it was very difficult to remove corrosion layers of HCl, but removing of NH3 corrosion layers was easy. It was caused by type of corrosion process (corrosion layers were influenced by time of corrosion process). This bachelor thesis is the start to find out conduct corrosion layers of brass in plasma treatment. In future, plasma treatment could be used to treatment of real archaeological artifacts.
|