Preparation of sample cross-sections and analysis by SIMS
Karlovský, Juraj ; Pechal, Radim (referee) ; Bábor, Petr (advisor)
This thesis studies possible methods of semiconductor sample measurement by SIMS, with emphasis on testing different measurement parameters and sample preparation. Part of this master thesis deals with the design of a modified sample holder compatible with the used ToF-SIMS$^{5}$ instrument, IONTOF company, which is capable of tilting the sample by defined angle. This holder enables sample preparation in the main chamber of the instrument without the need of transferring the sample between instruments, which limits the probability of sample contamination. This sample holder was tested by ion machining of TIGBT sample edge and by imaging of a crater edge, created in previous measurement. Edge termination structures prepared by different techniques were measured on the TIGBT samples. Further measurements with the goal of optimizing the depth resolution for thin layers were done on Molybdenum-Silicon-multilayer X-Ray Mirror. Part of the measurements was focused on comparing depth profiles measured at low temperatures. For these measurements the samples with Indium multilayers in GaN substrate were used.
|
|
|
Mechanical properties of doped piezoceramics based on BaTiO3
Zeman, Dominik ; Chlup, Zdeněk (referee) ; Drdlík, Daniel (advisor)
This master‘s thesis deals with study of basic physical, microstructural and mechanical properties of doped piezoceramic materials based on BaTiO3 prepared by electrophoretic deposition. The dopants used were rare earth oxides, i.e. Eu2O3, Er2O3, CeO2, Dy2O3 and Tb4O7 in amounts 1, 3 and 5 wt. %. The influence of dopants and their amount on density, phase composition, mean grain size, hardness, elastic modulus, fracture toughness, and flexural strength was examined. Suitable dopant choice enabled decrease in mean grain size and increase in relative density, hardness, elastic modulus, fracture toughness and flexural strength of sintered specimens. Relative densities up to 99 %, mean grain size below 1 m, hardness up to 13,1 GPa, elastic modulus up to 199 GPa, fracture toughness above 1 MPa·m1/2 and flexural strength above 115 MPa were achieved.
|
|
|
Ab initio calculation of doping in Ni2MnGa alloy
Janovec, Jozef ; Černý, Miroslav (referee) ; Zelený, Martin (advisor)
Cieľom tejto práce je teoretické štúdium systému Ni-Mn-Ga, vykazujúceho efekt magnetickej tvarovej pamäti. Pri výpočtoch bola použitá metóda Exaktných Mufiin-Tin Orbitálov v kombinácii s aproximáciou koherentného potenciálu vrámci Korringa-Kohn-Rostoker formalizmu. Totálna energia bola spočítaná pomocou metódy úplnej nábojovej hustoty. Skúmaný bol vplyv dopovania zinkom alebo kadmiom na totálne energie pozdĺž tetragonálnej deformačnej dráhy a následne na teplotu martenzitickej premeny TM a Curieho teplotu TC. Taktiež boli skúmané nestechiometrické zliatiny prebytkom Mn na úkor Ga. Výsledky predikujú nárast TM po všetkých pozorovaných substitúciách v podmriežke Ga a pokles TM po substitúciách v podmriežke Mn. Curieho teplotu znižujú všetky študované substitúcie s výnimkou zmeny magnetického usporiadania v martensite nestechiometrickej zliatiny.
|
|
|
Mechanical properties of doped piezoceramics based on BaTiO3
Zeman, Dominik ; Chlup, Zdeněk (referee) ; Drdlík, Daniel (advisor)
This master‘s thesis deals with study of basic physical, microstructural and mechanical properties of doped piezoceramic materials based on BaTiO3 prepared by electrophoretic deposition. The dopants used were rare earth oxides, i.e. Eu2O3, Er2O3, CeO2, Dy2O3 and Tb4O7 in amounts 1, 3 and 5 wt. %. The influence of dopants and their amount on density, phase composition, mean grain size, hardness, elastic modulus, fracture toughness, and flexural strength was examined. Suitable dopant choice enabled decrease in mean grain size and increase in relative density, hardness, elastic modulus, fracture toughness and flexural strength of sintered specimens. Relative densities up to 99 %, mean grain size below 1 m, hardness up to 13,1 GPa, elastic modulus up to 199 GPa, fracture toughness above 1 MPa·m1/2 and flexural strength above 115 MPa were achieved.
|
|
|
Preparation of sample cross-sections and analysis by SIMS
Karlovský, Juraj ; Pechal, Radim (referee) ; Bábor, Petr (advisor)
This thesis studies possible methods of semiconductor sample measurement by SIMS, with emphasis on testing different measurement parameters and sample preparation. Part of this master thesis deals with the design of a modified sample holder compatible with the used ToF-SIMS$^{5}$ instrument, IONTOF company, which is capable of tilting the sample by defined angle. This holder enables sample preparation in the main chamber of the instrument without the need of transferring the sample between instruments, which limits the probability of sample contamination. This sample holder was tested by ion machining of TIGBT sample edge and by imaging of a crater edge, created in previous measurement. Edge termination structures prepared by different techniques were measured on the TIGBT samples. Further measurements with the goal of optimizing the depth resolution for thin layers were done on Molybdenum-Silicon-multilayer X-Ray Mirror. Part of the measurements was focused on comparing depth profiles measured at low temperatures. For these measurements the samples with Indium multilayers in GaN substrate were used.
|
|
|
Ab initio calculation of doping in Ni2MnGa alloy
Janovec, Jozef ; Černý, Miroslav (referee) ; Zelený, Martin (advisor)
Cieľom tejto práce je teoretické štúdium systému Ni-Mn-Ga, vykazujúceho efekt magnetickej tvarovej pamäti. Pri výpočtoch bola použitá metóda Exaktných Mufiin-Tin Orbitálov v kombinácii s aproximáciou koherentného potenciálu vrámci Korringa-Kohn-Rostoker formalizmu. Totálna energia bola spočítaná pomocou metódy úplnej nábojovej hustoty. Skúmaný bol vplyv dopovania zinkom alebo kadmiom na totálne energie pozdĺž tetragonálnej deformačnej dráhy a následne na teplotu martenzitickej premeny TM a Curieho teplotu TC. Taktiež boli skúmané nestechiometrické zliatiny prebytkom Mn na úkor Ga. Výsledky predikujú nárast TM po všetkých pozorovaných substitúciách v podmriežke Ga a pokles TM po substitúciách v podmriežke Mn. Curieho teplotu znižujú všetky študované substitúcie s výnimkou zmeny magnetického usporiadania v martensite nestechiometrickej zliatiny.
|
guest ::