Issues of stopping the hydration of alkali-activated slag using organic substances
Chadima, Jan ; Novotný, Radoslav (referee) ; Bílek, Vlastimil (advisor)
This thesis deals with the stopping of hydration of alkali activated slag by organic solvents and investigates to what extent the selected organic solvent affects the results of the analyses. The solvents used were acetone, diethyl ether, ethanol, isopropanol and methanol, and this is because these are the most commonly used organic solvents in practice. Thermogravimetric analysis along with differential thermal analysis was used to assess the degree of influence of organic solvents on the alkali activated slag and Portland cement samples. Methanol and acetone affected the samples the most and the longer the sample was stored in the solvent, the more it reacted with the organic solvent. The adverse interaction of organic solvent was greatest for the Portland cement samples. Samples that were rinsed with diethyl ether prior to analysis had lower mass losses than samples that were not rinsed. In the case of alkali activated slag, it was found that the way in which the thermogravimetric results were affected by organic solvents was highly dependent on the activator used, with the smallest effect observed for Na2CO3 activation, while the largest effect was observed for NaOH activation at temperatures below 600 °C, and for higher temperatures for water glass activation.
|
|
Issues of stopping the hydration of alkali-activated slag using organic substances
Chadima, Jan ; Novotný, Radoslav (referee) ; Bílek, Vlastimil (advisor)
This thesis deals with the stopping of hydration of alkali activated slag by organic solvents and investigates to what extent the selected organic solvent affects the results of the analyses. The solvents used were acetone, diethyl ether, ethanol, isopropanol and methanol, and this is because these are the most commonly used organic solvents in practice. Thermogravimetric analysis along with differential thermal analysis was used to assess the degree of influence of organic solvents on the alkali activated slag and Portland cement samples. Methanol and acetone affected the samples the most and the longer the sample was stored in the solvent, the more it reacted with the organic solvent. The adverse interaction of organic solvent was greatest for the Portland cement samples. Samples that were rinsed with diethyl ether prior to analysis had lower mass losses than samples that were not rinsed. In the case of alkali activated slag, it was found that the way in which the thermogravimetric results were affected by organic solvents was highly dependent on the activator used, with the smallest effect observed for Na2CO3 activation, while the largest effect was observed for NaOH activation at temperatures below 600 °C, and for higher temperatures for water glass activation.
|