Electrospinning and characterization of fibrous structure for piezoapplications
Svobodová, Anežka ; Kaštyl, Jaroslav (referee) ; Částková, Klára (advisor)
The master’s thesis deals with the preparation and characterization of PVDF-based composite fibrous layers prepared by electrospinning. Ceramic particles TiO2, BaTiO3 and BCZT were used as fillers. The fibers were prepared containing 10, 20, 30, 40 and 50% of these particles and then their morphology, piezoactive phase representation and dielectric characterization were characterized. The effect of the presence of particles on the fiber diameter and on the crystallinity fraction of the polymer was shown. Particle size significantly influenced their distribution in the fibers. Piezoelectric particles further influenced the content of electroactive phases beta and gamma. The highest proportion of electroactive phases was determined in BaTiO3 filled fibers, which reached up to 98%. For the BaTiO3 filled fibers, the dielectric constant values were also measured, which reached lower values than expected due to the high porosity of the prepared fibers The as-prepared fibers can be considered promising not only for piezoapplications, therefore, optimization of their preparation and measurement of electrical characteristics will be further studied.
|
|
|
Electrospinning and characterization of fibrous structure for piezoapplications
Svobodová, Anežka ; Kaštyl, Jaroslav (referee) ; Částková, Klára (advisor)
The master’s thesis deals with the preparation and characterization of PVDF-based composite fibrous layers prepared by electrospinning. Ceramic particles TiO2, BaTiO3 and BCZT were used as fillers. The fibers were prepared containing 10, 20, 30, 40 and 50% of these particles and then their morphology, piezoactive phase representation and dielectric characterization were characterized. The effect of the presence of particles on the fiber diameter and on the crystallinity fraction of the polymer was shown. Particle size significantly influenced their distribution in the fibers. Piezoelectric particles further influenced the content of electroactive phases beta and gamma. The highest proportion of electroactive phases was determined in BaTiO3 filled fibers, which reached up to 98%. For the BaTiO3 filled fibers, the dielectric constant values were also measured, which reached lower values than expected due to the high porosity of the prepared fibers The as-prepared fibers can be considered promising not only for piezoapplications, therefore, optimization of their preparation and measurement of electrical characteristics will be further studied.
|
guest ::