Assessment of probable causes of corrosion damage of a glass-shaping mould
Jíša, Jakub ; Pantělejev, Libor (referee) ; Man, Ondřej (advisor)
The aim of this thesis was to characterize briefly the issue of electrochemical corrosion in the aquatic environment with a focus on cast-iron corrosion and then decide whether the observed damage to the glass-forming mold could arise in the course of two days. A simple corrosion experiment was made in which samples of cast-iron were exposed to the shower of water for 48 hours. Corrosion damage under simulated conditions did not reach the level of damage of the mold.
|
|
|
Design of Hole Punch
Kreidlová, Tereza ; Křenek, Ladislav (referee) ; Sládek, Josef (advisor)
The presented bachelor thesis is focused on the design of cast-iron hole punch. This thesis deals with an analysis of current and historical products, basic technical characteristics and then describes the proposed design solution. The aim of this work is to increase the aesthetics and ergonomics of the hole punch’s handrail with the use of interesting material and to improve functionality of the whole product.
|
|
| |
|
|
Design of Hole Punch
Kreidlová, Tereza ; Křenek, Ladislav (referee) ; Sládek, Josef (advisor)
The presented bachelor thesis is focused on the design of cast-iron hole punch. This thesis deals with an analysis of current and historical products, basic technical characteristics and then describes the proposed design solution. The aim of this work is to increase the aesthetics and ergonomics of the hole punch’s handrail with the use of interesting material and to improve functionality of the whole product.
|
|
| |
|
|
Assessment of probable causes of corrosion damage of a glass-shaping mould
Jíša, Jakub ; Pantělejev, Libor (referee) ; Man, Ondřej (advisor)
The aim of this thesis was to characterize briefly the issue of electrochemical corrosion in the aquatic environment with a focus on cast-iron corrosion and then decide whether the observed damage to the glass-forming mold could arise in the course of two days. A simple corrosion experiment was made in which samples of cast-iron were exposed to the shower of water for 48 hours. Corrosion damage under simulated conditions did not reach the level of damage of the mold.
|
guest ::