Kocúrek, Ondřej ; Novák, Zdeněk (referee) ; Humár, Anton (advisor)
This thesis deals with a summary of different types and characteristics of coatings used for increasing the lifetime of cemented carbide tools. Besides, the thesis includes solving the issue regarding edge chipping during machining interrupted pipe ends at the pipe line, selecting a new type of indexable inserts and indexable inserts holders to increase line productivity and decrease tool costs in the related operation.
|
|
| |
|
|
Technological Design for a Motorcycle Brake
Smílek, Lukáš ; Fiala, Zdeněk (referee) ; Kalivoda, Milan (advisor)
This thesis deals with the design of technological components for drum brake motorcycle. The introduction deals with the history of development of braking systems and their basic distribution.The documentation includes technological production process, the building of NC program in 3D design software and technical-economic evaluation.
|
|
|
Durability testing of replaceable inserts in cylindrical turning of carbon steel
Smolík, Martin ; Vítek, Jiří (referee) ; Sedlák, Josef (advisor)
The thesis deals with the problems in the field of durability testing of replaceable inserts for longitudinal steel turning. The main objective of the thesis is the analysis of the cutting process based on the results of the performed cutting tests. The cutting tests will be carried out comparatively by testing pairs of inserts, compared to each other. Wear observation is carried out by optical method using a workshop microscope and special software designed to process the acquired images. The output of the work will be an illustration of the different behaviour of the standard and the upgraded set of cutting inserts under different configurations of cutting conditions. The work provides a comprehensive view of the cutting tool testing process and quantifies the degree of influence of the various factors entering into the cutting edge wear process.
|
|
|
Effect of cutting inserts surface treatment on turning durability of stainless steel
Filip, Jiří ; Vítek, Jiří (referee) ; Sedlák, Josef (advisor)
The diploma thesis deals with the testing of coated carbide inserts with different types of surface treatments. The testing was conducted using longitudinal turning technology under constant cutting conditions, and the workpiece material used was austenitic corrosion-resistant steel. The aim was to analyze the wear progress of the cutting edges after predetermined time intervals and to determine the resulting durability of the tested inserts. During the testing, the cutting edges of the tools broke off and the required durability was not achieved. After a thorough examination of the workpiece material, a significant amount of unevenly distributed inclusions was found in the steel structure, which proved to be the main cause of the insert breakage. Therefore, it was decided to perform a replacement test using material from a new supplier. Material analysis of the newly delivered steel showed a significantly better purity of the structure, which was positively reflected in the results of the second test, in which there was no brittle fracture of the edge in any case and the tested samples reached the required durability. The best results were obtained with samples treated on flanks using a new surface treatment method developed by Dormer Pramet s.r.o. After completing the tests, an adhesion test of the coating to the tool substrate was performed using the Rockwell method. Based on microscopic images that revealed partial delamination of the coating, it was evaluated that the quality of the deposited layer was not quite optimal. In a technical and economical evaluation were determined the potentially saved costs when using the experimental cutting insert compared to the reference plate A.
|
|
|
Optimization of indexable inserts use in production line
Kocúrek, Ondřej ; Novák, Zdeněk (referee) ; Humár, Anton (advisor)
This thesis deals with a summary of different types and characteristics of coatings used for increasing the lifetime of cemented carbide tools. Besides, the thesis includes solving the issue regarding edge chipping during machining interrupted pipe ends at the pipe line, selecting a new type of indexable inserts and indexable inserts holders to increase line productivity and decrease tool costs in the related operation.
|
|
|
Technological Design for a Motorcycle Brake
Smílek, Lukáš ; Fiala, Zdeněk (referee) ; Kalivoda, Milan (advisor)
This thesis deals with the design of technological components for drum brake motorcycle. The introduction deals with the history of development of braking systems and their basic distribution.The documentation includes technological production process, the building of NC program in 3D design software and technical-economic evaluation.
|
|
| |
guest ::