Microstructure and Texture of Titanium Prepared by Powder Metallurgy
Kozlík, Jiří ; Stráský, Josef (advisor) ; Chráska, Tomáš (referee)
Bulk commercially pure titanium was prepared by powder metallurgy, namely by cryogenic milling and spark plasma sintering, with aim to produce ultra-fine grained material with enhanced strength. The microstructure of milled powders was investigated in detail by a novel method called transmission EBSD, which allowed the first direct observation of texture within the powder particles. This texture is similar to rolling texture, because of the similar nature of the defor- mation during milling. Microstructure observations revealed grains with the size under 100 nm. The influence of sintering parameters on material properties were studied by scan- ning electron microscopy including EBSD, X-ray diffraction and by microhardness measurements. The trade-off relationship between porosity and grain size was identified, fully dense material with ultra-fine grained microstructure could not be produced. Increased oxygen content was identified as a main strengthening factor, while porosity has significant deteriorating effect on mechanical properties. The texture of powder was retained in the bulk material. The possibility of stabilizing the microstructure by mechanical alloying of Ti with yttrium oxide nanoparticles was investigated with mixed results. The stabiliza- tion was successful, but several issues...
|
|
|
Oxygen-strengthened biomedical beta titanium alloys
Preisler, Dalibor ; Stráský, Josef (advisor) ; Kužel, Radomír (referee)
Oxygen strengthened biomedical beta titanium alloys Beta titanium alloy Ti-35Nb-6Ta-7Zr-0.7O (wt. %) exhibits a low Young's modulus and high strength thanks to interstitial strengthening effect of oxygen. These mechanical properties are promising for implant production. In this thesis, the aforementioned alloy is thoroughly studied in conditions prepared by various thermomechanical treatments, namely: material after casting, hot compression testing, die-forging, hot rolling and finally, cold-swaged and annealed condition. Mechanical properties and microstructure of prepared conditions are studied with special interest of enhancing the fatigue performance that is poor after casting due to porosity and large grains. The hot rolling was shown to improve the fatigue performance significantly, mainly through grain refinement. It is shown that by combining the effects of cold-swaging and recrystallization annealing, extensive refinement of grain structure can be achieved. Industrial aspects of implant production by the studied methods were discussed. In the second part of the thesis, the possibility of lowering the Young's modulus by reducing the beta phase stability (by reducing of Nb and Ta content), while retaining high strength caused by high interstitial oxyen content is explored. Several alloys were...
|
|
|
Morphology and hardness of particles of titanium powder prepared by cryogenic milling
Ibragimov, Ilya ; Stráský, Josef (advisor) ; Janeček, Miloš (referee)
The effect of cryogenic milling on morphology and microhardness of titanium powder was investigated. Initial powder of commercially pure titanium was subjected to cryogenic milling in liquid argon (LAr) using two different milling speeds. Prepared powders were subsequently cleaned by ethanol. The cleaning procedure was done in two ways: in the air and in the inert atmosphere in the glovebox. Particle size and morphology were investigated my scanning electron microscopy and subsequent automated image analysis. Microhardness of powder particles was determined by Vickers hardness measurement using small loads. The milling did not cause significant powder refiniment, while the shape of powder particles changes substantially. Milling speed affected particle shape and powder contamination. Application of stearic acid as the processing control agent prevented cold-welding of powder particles, but contaminated the powder by oxygen and hydrogen. Stearic acid could be successfully removed by cleaning in ethanol. The using of glovebox for cleaning did not have significant effect on the resultiing contamination.
|
|
|
Microstructure and mechanical properties of ultra-fine grained titanium alloys
Václavová, Kristína ; Stráský, Josef (advisor)
Title: Microstructure and mechanical properties of ultra-fine grained titanium alloys Author: Bc. Kristína Václavová Department / Institute: Department of Physics of Materials Supervisor of the master thesis: PhDr. RNDr. Josef Stráský, Ph.D. Abstract: Metastable β-Ti alloys Ti-15Mo and Ti-6.8Mo-4.5Fe-1.5Al (TIMETAL LCB) were subjected to severe plastic deformation by high pressure torsion. Microhardness of Ti-15Mo and TIMETAL LCB alloys increases with increasing inserted deformation, i.e. with increasing number of HPT rotations and also with increasing distance from the centre of the sample. The highest microhardness after HPT exceeds significantly the microhardness of two-phase α + β heat-treated material. Increasingly deformed microstructure was also demonstrated by scanning electron microscopy and by electron back-scattered diffraction (EBSD). Significant twinning was observed in both studied alloys. Mechanism of multiple twinning contributes notably to the fragmentation of grains and thus to the refinement of the microstructure. Defect structure in Ti-15Mo alloy was studied by positron annihilation spectroscopy. It was proved that dislocations are the only detectable defects in the material by positron annihilation spectroscopy and that dislocation density increases with the number of HPT revolution and...
|
|
|
Metastable beta titanium alloys for biomedical use
Preisler, Dalibor ; Stráský, Josef (advisor) ; Janeček, Miloš (referee)
In this work the effect of die-forging and annealing on the mechanical properties and microstructure of biocompatible metastable alloy Ti-35.3Nb-7.3Zr -5.7Ta-0.7O (wt. %) was studied. Light and scanning electron microscopy, microhardness tests and tensile tests were used to study all prepared conditions. As-cast and as-annealed conditions showed chemical inhomogeneities exhibited as dendritic structure, grains with size of hundreds of micrometers and numerous pores having size of units of micrometers. Precipitation of alpha phase particles was negligible in as-annelaed conditions and only grain boundary alpha paticles formed. Die-forged condition showed grain sizes in the wide range of hundreds of micrometers down to micrometers. Both as-annealed and die-forged conditions showed increased microhardness compared to as-cast condition, but there were no significant differences between different annealing conditions. Yield stress of 870 MPa was found for as-cast condition while as-forged condition exhibited even higher yield stress of 1120 MPa. In both conditions, good room-temperature ductility was demonstrated. Due to its high strength, this alloy is perspective for manufacturing of joint implants.
|
|
|
Titanium and titanium alloys prepared by cryogenic milling
Kozlík, Jiří ; Stráský, Josef (advisor) ; Janeček, Miloš (referee)
Ultra-fine grained materials are presently thoroughly investigated due to their enhanced mechanical properties. Cryogenic milling is one of the severe plastic deformation methods, which allow production of these materials. Titanium powder was processed by cryogenic milling in liquid nitrogen and argon and consequently consolidated via spark plasma sintering method. In this work, the influence of milling conditions (liquid nitrogen vs. liquid argon, material of balls, duration and speed of milling, usage of stearic acid) on size and shape of powder particles, contamination and mechanical properties was investigated. Particle size reduction was generally not observed, while their morphology changed significantly. Using liquid nitrogen as a cooling medium leads to strong contamination of prepared material and consequently to its hardening and embrittlement. Stearic acid supresses cold welding of particles during milling and enhances its efficiency. It is possible to eliminate stearic acid from powder by cleaning in acetone before sintering, to prevent contamination of processed material. Microhardness increased, depending on milling efficiency (in liquid argon), from original 178 HV to 200-300 HV range. Increase of yield and ultimate stength was observed in compression tests while maintaining ductility....
|
|
| |
|
|
Wealth inequality in dynamic stochastic general equilibrium models
Troch, Tomáš ; Stráský, Josef (advisor) ; Gregor, Martin (referee)
in English In my diploma thesis I propose a dynamic stochastic general equilibrium model to describe economic inequality. The model combines two approaches that were traditionally used to model inequality - first, it features two classes of agents that differ in their ownership of capital and second, each class consists of heterogeneous agents who are subject to uninsurable idiosyncratic shocks. This combination allows the two classes to behave in a fundamentally different way while maintaining the individual character of agents in the economy - a feature that has not been modeled before but which adequately describes the empirical reality. I show that the model with classical RBC structure and a single wage underestimates the observed inequality. When the wage differential is introduced through different taxation of the two classes, the model matches empirical inequality much better. Further I argue that the government can significantly reduce inequality at a relatively small cost in terms of output lost. Finally using Theil coefficient decomposition, I show how much of the total inequality is attributable to between-class and within-class inequalities.
|
|
|
Optimization of properties of Ti based alloys for biomedical and structural applications
Stráský, Josef ; Janeček, Miloš (advisor) ; Hadzima, Branislav (referee) ; Karlík, Miroslav (referee)
Title: Optimization of properties of Ti based alloys for biomedical and structural applications Author: Josef Stráský Department / Institute: Department of Physics of Materials Supervisor of the doctoral thesis: Assoc. Prof. Miloš Janeček, Ph.D. Abstract: Titanium alloys belong to the mostly used biomaterials for orthopaedic implants. Advanced surface treatments of Ti alloys for orthopaedic use and newly developed biomedical beta-Ti alloys are investigated in this thesis. Wide spectrum of experimental techniques was employed in order to correlate material processing, microstructure and mechanical properties. Electric discharge machining was used as a biocompatibility enhancing surface treatment of Ti-6Al-4V alloy, but the treated material suffered from the poor fatigue performance. Two subsequent surface treatments - chemical etching and shot- peening - were proposed and it was shown that their combination significantly improves the fatigue performance of the material making it applicable in orthopaedics. This process was patented in the Czech Republic. The thesis further reviews complex problematic of biocompatible beta-Ti alloys. Several new biocompatible beta-Ti alloys were designed on the basis of Ti-Nb-Zr-Ta quaternary alloy. The effect of Fe, Si and O additions on microstructure, elastic modulus and...
|
|
|
Experimentální studium ultrajemnozrnných slitin Ti pro využití v biomedicíně
Václavová, Kristína ; Stráský, Josef (advisor) ; Šíma, Vladimír (referee)
In the present work the microstructure evolution of Ti-6Al-7Nb alloy prepared by high pressure torsion (HPT) and equal channel angular pressing (ECAP) was studied by scanning electron microscopy, microhardness measurements and electrical resistance measurements. Electron microscopy showed a bimodal structure of the alloy and deformed structure after HPT. Microhardness increased with the increasing number of turns of high pressure torsion. Electron back-scattered diffraction figured out that the grain misorientations are not random. Changes in the electrical resistance of the alloy prepared by ECAP showed irreversible process after heating above 450řC.
|