Assessment of Crack Stability in a Quasi-brittle Particle Composite
 Malíková, Lucie ; Klusák, Jan ; Keršner, Z.
Fracture behaviour of a crack in a particle (silicate based) composite is studied. The crack propagation depends not only on mutual elastic mismatch of matrix and aggregate but also the influence of the interfacial transition zone (ITZ) between the matrix and the aggregate is discussed. Various combinations of materials and geometry of matrix, aggregate and ITZ can improve or degrade fracture properties of the composite. Extensive numerical simulations on a basic 3-point-bending cracked specimen via the finite element method are performed in order to analyze the stress field near the crack tip. Linear elastic fracture mechanics approach is utilized in order to assess the crack stability and summarize several conclusions.
Úplný záznam
Odhad kritického napětí pro poškození povrchové vrstvy
 Náhlík, Luboš
V příspěvku je studováno chování trhliny šířící se v okolí rozhraní dvou materiálů. Jsou analyzovány podmínky stability trhliny s vrcholem na rozhraní dvou materiálů za předpokladu platnosti lineární elastické lomové mechaniky. Kritérium stability je formulováno na základě koncepce hustoty deformační energie a je použito pro odhad kritického aplikovaného napětí při kterém se trhlina začne šířit z rozhraní do druhého materiálu. Je ukázáno, že kritické napětí silně závisí na lomové houževnatosti druhého materiálu a na odpovídajících bi-materiálových parametrech.
Úplný záznam
Estimation of the Critical Stress for Failure of a Protective Layer
 Náhlík, Luboš ; Knésl, Zdeněk
This contribution describes a study of the behaviour of a crack growing in a protective layer and penetrating through an interface into a substrate. Special attention is devoted to a crack touching the interface. Conditions for the stability of a crack terminating at the interface between two materials are analyzed. The problem is studied under the assumptions of linear-elastic fracture mechanics. A new tentative criterion of stability based on application of the strain energy density concept is formulated and applied to the problem. The suggested criterion is used to estimate the critical applied stress for the failure of a substrate caused by a crack growing through the protective layer. It is shown that the critical stress may strongly depend on the fracture toughness of the substrate and on the bi-material parameters.
Úplný záznam
Analýza růstu trhliny přes rozhraní dvou různých materiálů pomocí otevření trhliny
 Bareš, Pavel ; Knésl, Zdeněk
V příspěvku je analyzováno chování trhliny šířící se přes bi-materiálové rozhraní. Jsou zde formulovány podmínky stability trhliny ležící na rozhraní. Jako řídící veličina je použita hodnota otevření kořene trhliny. Získané výsledky jsou porovnány s hodnotami určenými pomocí jiných kritérií. Odpovídající výpočty jsou provedeny metodou konečných prvků (MKP) systémem ANSYS.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English