Welding of deep-drawing steels with protective layer by laser-TIG hybrid technology
Brehovský, Patrik ; Sigmund, Marian (oponent) ; Mrňa, Libor (vedoucí práce)
The diploma thesis focuses on laser welding of extra deep-drawn steel sheet according to the standard WSS-M1A365-A14 with a protective zinc surface layer. A 0,9 mm thick steel sheet with a zinc layer with coating weight 50 g · m^-2 is welded by a hybrid welding method Laser-TIG. The laser, as the primary energy source, is used for welding the material. The arc, provided by a non-melting tungsten electrode, is used for preheating the material for melting and evaporation of the zinc layer. Based on the initial experiments, the magnitude of the laser power with the welding speed was chosen as a constant parameter. The magnitude of the electric current, as the variable parameter, was set up to 0, 20, 30 and 40 ampers for welding the lap and the butt welds. Only one piece of the each weld type combination was made. The welds were afterwards tested to verify their quality and material properties. The first differences between laser welding with or without TIG preheating were visible during the experiment. The positive effects of the laser welding with preheating by TIG were confirmed. The material properties of the joints achieved better values and a influence of the welding defects on the quality of the joints was reduced. The Laser-TIG is a good choice for welding galvanized steel sheets in the mass production of automotive industry and it could be improved by more researches.
|
|
|
Využití předehřevu elektrickým obloukem při laserovém svařování ocelí s vyšším obsahem uhlíku
Mach, Martin ; Sigmund, Marian (oponent) ; Mrňa, Libor (vedoucí práce)
Diplomová práce je zaměřena na studium využití předehřevu elektrickým obloukem, v tomto případě zdroje TIG, při laserovém svařování oceli s vyšším obsahem uhlíku, konkrétně pro tuto práci oceli 1.1191 tloušťky 2 mm. Na základě vypočtení uhlíkového ekvivalentu byla určena velikost předehřevu na 208 °C. Svařovací parametry byly zvoleny na základě prvních experimentů. V experimentální části byly vzorky svařeny laserem s předehřevem pomocí zdroje TIG, které posléze byly podrobeny zkoušce tahem, mikrotvrdosti podle Vickerse, makrostruktury a mikrostruktury. Použitím druhého zdroje tepla byla rozšířena tepelně ovlivněná oblast u vzorků. Vzorky, které praskly uprostřed svaru při tahové zkoušce, byly tepelně ovlivněny řezáním vzorků. Zbylé vzorky praskly v základním materiálu, tudíž vytvořený svar byl kvalitní. Kombinace svařování laserem s předehřevem elektrickým obloukem TIG je velice produktivní metoda oproti konvenčním metodám a jedním z mála řešení předehřevu pro laserové svařování. Jedná se o prvotní experimenty využití elektrického oblouku TIG pro předehřev při laserovém svařování, na které bude navazovat další výzkum, převážně pro automobilový průmysl.
|
|
|
Welding of deep-drawing steels with protective layer by laser-TIG hybrid technology
Brehovský, Patrik ; Sigmund, Marian (oponent) ; Mrňa, Libor (vedoucí práce)
The diploma thesis focuses on laser welding of extra deep-drawn steel sheet according to the standard WSS-M1A365-A14 with a protective zinc surface layer. A 0,9 mm thick steel sheet with a zinc layer with coating weight 50 g · m^-2 is welded by a hybrid welding method Laser-TIG. The laser, as the primary energy source, is used for welding the material. The arc, provided by a non-melting tungsten electrode, is used for preheating the material for melting and evaporation of the zinc layer. Based on the initial experiments, the magnitude of the laser power with the welding speed was chosen as a constant parameter. The magnitude of the electric current, as the variable parameter, was set up to 0, 20, 30 and 40 ampers for welding the lap and the butt welds. Only one piece of the each weld type combination was made. The welds were afterwards tested to verify their quality and material properties. The first differences between laser welding with or without TIG preheating were visible during the experiment. The positive effects of the laser welding with preheating by TIG were confirmed. The material properties of the joints achieved better values and a influence of the welding defects on the quality of the joints was reduced. The Laser-TIG is a good choice for welding galvanized steel sheets in the mass production of automotive industry and it could be improved by more researches.
|
|
|
Využití předehřevu elektrickým obloukem při laserovém svařování ocelí s vyšším obsahem uhlíku
Mach, Martin ; Sigmund, Marian (oponent) ; Mrňa, Libor (vedoucí práce)
Diplomová práce je zaměřena na studium využití předehřevu elektrickým obloukem, v tomto případě zdroje TIG, při laserovém svařování oceli s vyšším obsahem uhlíku, konkrétně pro tuto práci oceli 1.1191 tloušťky 2 mm. Na základě vypočtení uhlíkového ekvivalentu byla určena velikost předehřevu na 208 °C. Svařovací parametry byly zvoleny na základě prvních experimentů. V experimentální části byly vzorky svařeny laserem s předehřevem pomocí zdroje TIG, které posléze byly podrobeny zkoušce tahem, mikrotvrdosti podle Vickerse, makrostruktury a mikrostruktury. Použitím druhého zdroje tepla byla rozšířena tepelně ovlivněná oblast u vzorků. Vzorky, které praskly uprostřed svaru při tahové zkoušce, byly tepelně ovlivněny řezáním vzorků. Zbylé vzorky praskly v základním materiálu, tudíž vytvořený svar byl kvalitní. Kombinace svařování laserem s předehřevem elektrickým obloukem TIG je velice produktivní metoda oproti konvenčním metodám a jedním z mála řešení předehřevu pro laserové svařování. Jedná se o prvotní experimenty využití elektrického oblouku TIG pro předehřev při laserovém svařování, na které bude navazovat další výzkum, převážně pro automobilový průmysl.
|