Redistribuce hliníku a uhlíku ve svarech ocelí v intervalu teplot 500-1100oC (1,15 hm.% Al)
Stránský, K. ; Million, Bořivoj ; Foret, R. ; Michalička, Petr ; Rek, A.
Měření redistribuce Al, Cr, Fe, Ni, C ve svarových spojích nelegované oceli 12050+1,15Al a vysokolegované Cr-Ni oceli 17242 v teplotním intervalu 500-1100oC bylo provedeno na analytickém komplexu JEOL JXA 8600/KEVEX. Byly stanoveny difuzní koeficienty C, Al, Cr, Fe, Ni a diskutovány vztahy mezi nimi.
|
|
Long-Time Oxidation of gammaFe and LH15 Steel at High Temperatures in Air
Kučera, Jaroslav ; Adamaszek, K. ; Jurasz, Z.
The results of surface oxidation and decarburizatin of (Fe, C, Mn, Si, Cr, Ni) steels are reported. The oxidation anneals were carried out at temperatures T = 940, 980, 1020, 1060, 1100 oC. The time course of Fe and of steels oxidation is expressed by parabolic law. The surface oxidation is accompanied by decarburization of surface steel layers. The evaluation of measured carbon concentration profiles N(C,x,t) yields diffusion coefficients D(C,T). Oxidation coefficients kp(T) are linearly proportional to D(C,T).
|
| |
| |
|
OXIDATION OF Fe AND STEELS AT HIGH TEMPERATURES
Kučera, Jaroslav ; Adamaszek, K. ; Hajduga, M.
The results of surface oxidation and decarburization of (Fe, C, Mn, Si, Cr, Ni) steels are reported. The oxidation anneals were carried out at temperatures T = 940, 980, 1020, 1060, 1100 °C. The time course of Fe and of steels oxidation is expressed by parabolic law l = kp . The surface oxidation is accompanied by decarburization of surface steel layers. The evaluation of measured carbon concentration profiles N(C,x,t) yields diffusion coefficients D(C,T). Oxidation coefficients kp(T) are linearly proportional to D(C,T).
|
|
LONG-TIME OXIDATION OF .gamma.Fe AND LH15 STEEL AT HIGH TEMPERATURES IN AIR
Kučera, Jaroslav ; Adamaszek, K. ; Jurasz, Z.
The investigation of long-time oxidation of gFe and of low alloyed steel LH15 in ambient air is reported. The specimens of gFe had the form of wires with diameter f = 3.0 mm. The relative weight gain Dw/w of these specimens grows in the course of oxidation anneal due to the oxides FeO, Fe3O4, Fe2O3 formation. The weight gain is stopped at very long time period t of oxidation anneals. This phenomenon is denoted as saturation effect. The same effect was observed in the case of oxidation of specimens made from low alloyed steel LH15. The specimens had the form of cylinders with diameter .fi. = 10 mm.
|
|
Současná difuze hliníku, uhlíku, chromu, železa a niklu ve svarech ocelí v rozmezí teplot 500 až 1100°C
Stránský, K. ; Million, Bořivoj ; Foret, R. ; Rek, A. ; Michalička, Petr
V příspěvku jsou uvedeny výsledky měření současné difuze hliníku, uhlíku, chromu, železa a niklu ve svarových spojích nelegované oceli typu 12050 se zvýšenou koncentrací hliníku a vysokolegované austenitické CrNi oceli 17242.
|
| |
| |
| |