METALLURGY AND PROPERTIES OF ADVANCED NiAl-Mo EUTECTICS
Barták, Tomáš ; Kuchařová, Květa ; Záležák, Tomáš ; Dlouhý, Antonín
A NiAl-Mo eutectic alloy was melt from 99,99% purity components and cast by the drop casting technique. The drop-cast ternary alloy (nominal composition of Ni-45Al-9Mo at. %), was re-melted and directionally solidified using a high temperature optical floating zone furnace. A resulting in-situ composite consists of Ni-45,2Al matrix and Mo-10Al-4Ni fibers, all in at. %. The volume fraction of 14% Mo-fibers stems from the eutectic composition. Spacing and a diameter of Mo-fibers can be controlled within certain limits using different growth rates of the crystals. Microstructural parameters of the as-cast crystals were assessed by light microscopy, scanning and transmission electron microscopy. Backscatter diffraction shows that the NiAl-matrix and the Mo-fibers are both < 001 >-oriented with respect to the axis of the cylindrical rods. Preliminary creep experiments confirmed an immense improvement of high temperature strength due to the fine distribution of Mo-fibres. The amount of strengthening in terms of minimum creep rate can be as high as 7 orders of magnitude. Post-mortem transmission electron microscopy experiments provided evidence that creep in the temperature range of 800-900 degrees C results in an extensive formation of subgrain boundaries. The strengthening effect is very likely associated with the reactions between subgrain boundaries and fine Mo-fibres.
|
|
|
METALLURGY AND PROPERTIES OF ADVANCED NiAl-Mo EUTECTICS
Barták, Tomáš ; Kuchařová, Květa ; Záležák, Tomáš ; Dlouhý, Antonín
A NiAl-Mo eutectic alloy was melt from 99,99% purity components and cast by the drop casting technique. The drop-cast ternary alloy (nominal composition of Ni-45Al-9Mo at. %), was re-melted and directionally solidified using a high temperature optical floating zone furnace. A resulting in-situ composite consists of Ni-45,2Al matrix and Mo-10Al-4Ni fibers, all in at. %. The volume fraction of 14% Mo-fibers stems from the eutectic composition. Backscatter diffraction shows that the NiAl-matrix and the Mo-fibers are both < 001 >-oriented with respect to the axis of the cylindrical rods. Preliminary creep experiments confirmed an immense improvement of high temperature strength due to the fine distribution of Mo-fibres. The amount of strengthening in terms of minimum creep rate can be as high as 7 orders of magnitude. Post-mortem transmission electron microscopy experiments provided evidence that creep in the temperature range of 800 - 900 degrees C results in an extensive formation of subgrain boundaries. The strengthening effect is very likely associated with the reactions between subgrain boundaries and fine Mo-fibres.
|
|
|
3D modelování dislokačních procesů
Záležák, Tomáš
Příspěvek představuje 3D model vývoje dislokací za vysokých teplot. Model využívá lineární teorii elasticity. Obecná křivka je nahrazena lomenou čarou. Pomocí Peach-Koehlerova vzorce jsou vypočítány hnací síly pro jednotlivé segmenty. Ty jsou určeny vlastním napěťovým polem v soustavě a vnějším aplikovaným napětím, popř. self-interakcí. Pohyb jednotlivých segmentů je aproximován teplotně závislou lineární funkcí hnací síly. Model umožňuje vložit do systému kulové precipitáty, okrajová podmínka zamezuje průniku dislokačních čar do částic. Model rovněž zohledňuje topologické změny křivky zapříčiněné anihilací dislokací, např. ve Frankově-Readově zdroji či při pronikání čar mezi precipitáty. Model využívá symetrii úlohy a umožňuje zvolit menší a jednodušší elementární buňku simulace, a provést tak rychlejší a stabilnější výpočet. Dále jsou představeny výsledky simulací pro soustavyněkolika dislokačních smyček za přítomnosti souměrně umístěných čtveřic kulových precipitátů.
|
host ::
RSS.