Fractural based microstructural damane evaluation in Ni-based superalloy gas turbine blades
 Tarafder, M. ; Dlouhý, Ivo ; Hore, S. ; Das, S. K.
A fractal based evaluation of microstructural damage in Ni based superalloy cast IN 738 LC used in gas turbine blades is presented in the paper. Non-destructive in-situ replica method was used without damaging the blades for the evaluation of microstructure. The theoretical life of the stator blades of the gas turbine, which was exposed to temperature varying between 1060°C to 1100°C, was approximately 100,000 hours. In order to assess the suitability of the stator blades after 50% of the service life, fractal based microstructural damage evaluation has been conducted. The fractal dimensions of the in situ metallographic images can be correlated to the progressive deterioration of hardness at various locations of the blades. The extent of damage is inversely proportional to the fractal dimension. For fractal dimension below 2.4, the material can be classified as substantially damaged.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English