Comparison of dynamic modulus of elasticity repair materials exposed to thermal stress
Munduchová, Markéta ; Jakubík, Aleš (referee) ; Brožovský, Jiří (advisor)
Diploma thesis is composed of theoretical and practical part. In theoretical part there are findings related to structure changes of concrete exposed to high temperatures. Models used to simulate high temperature exposure of concrete are described in this thesis. Evaluation of internal structure damage is appropriate by using non-destructive methods, which determine dynamic modulus of elasticity in compression and tension. These methods includes ultrasonic impulse method and resonation method and therefore research was made of articles contains these methods. In experimental part of diploma thesis the test specimens was made from repair materials from UTHD and commercially produced repair materials. The test specimens were subjected to thermal load: 200, 400, 600, 800 °C. Damage of internal structure was examined by ultrasonic impulse method and resonation method.
|
|
|
Assessment of the state of wood in the construction and evaluation of the usefulness of non-destructive testing methods
Munduchová, Markéta ; Vaněrek, Jan (referee) ; Brožovský, Jiří (advisor)
This bachelor's thesis consists of theoretical and experimental part. In the theoretical part there are given findings regarding on structure of wood, its basic properties and durability. The following describes the wood defects, influence of wood pests and fungi, types of wooden structures, climatic conditions, chemical corrosion and mechanical damage to the wood. Evaluation of the status of wood in the structures is appropriate by using non-destructive methods, therefore was performed research articles on these methods. Non-destructive methods are used: visual, hardness tests, electrical, radiation, optical and moisture determination. Experimental part of the bachelor's thesis is focused on ultrasonic impulse method, that can detect defects or damage in the wood mass that depends on the speed of ultrasonic impulse. For a reliable interpretation of the results it is appropriate to combine non-destructive methods when assessing status of wood structure.
|
|
|
Comparison of dynamic modulus of elasticity repair materials exposed to thermal stress
Munduchová, Markéta ; Jakubík, Aleš (referee) ; Brožovský, Jiří (advisor)
Diploma thesis is composed of theoretical and practical part. In theoretical part there are findings related to structure changes of concrete exposed to high temperatures. Models used to simulate high temperature exposure of concrete are described in this thesis. Evaluation of internal structure damage is appropriate by using non-destructive methods, which determine dynamic modulus of elasticity in compression and tension. These methods includes ultrasonic impulse method and resonation method and therefore research was made of articles contains these methods. In experimental part of diploma thesis the test specimens was made from repair materials from UTHD and commercially produced repair materials. The test specimens were subjected to thermal load: 200, 400, 600, 800 °C. Damage of internal structure was examined by ultrasonic impulse method and resonation method.
|
|
|
Assessment of the state of wood in the construction and evaluation of the usefulness of non-destructive testing methods
Munduchová, Markéta ; Vaněrek, Jan (referee) ; Brožovský, Jiří (advisor)
This bachelor's thesis consists of theoretical and experimental part. In the theoretical part there are given findings regarding on structure of wood, its basic properties and durability. The following describes the wood defects, influence of wood pests and fungi, types of wooden structures, climatic conditions, chemical corrosion and mechanical damage to the wood. Evaluation of the status of wood in the structures is appropriate by using non-destructive methods, therefore was performed research articles on these methods. Non-destructive methods are used: visual, hardness tests, electrical, radiation, optical and moisture determination. Experimental part of the bachelor's thesis is focused on ultrasonic impulse method, that can detect defects or damage in the wood mass that depends on the speed of ultrasonic impulse. For a reliable interpretation of the results it is appropriate to combine non-destructive methods when assessing status of wood structure.
|