Hybride binders based on the high-calcium ash
Hubáček, Václav ; Cába, Vladislav (referee) ; Koplík, Jan (advisor)
The goal of this bachelor´s thesis was to develop a hybrid binder based on high calcium fly ash with the focus on addition of Portland cement, observation of hydration process, measurement of mechanichal properties, identification of hydration products and comparation with Portland cement. Hybrid binder was developer by adding different amounts of Portland cement to the selected mixture of high calcium fly ash activated by sodium hydroxide. Setting times and flexural strength and compressive strength were measured for these hybrid binders. Afterwards one type of hybrid binder was selected for more analyses (XFR, XRD, SEM/EDS and isothermic calorimetry). These analyses were also used for a sample of Portland cement and alkali activated high calcium fly ash and afterwards these three samples were compared between each other. The collected data show that the compositions of the activated fly ash and hybrid binder are very similar and the addition of Portland cement to the mixture has only a minor impact. Main hydration product for both of them was ettringite. Addition of Portland cement to the activated high calcium fly ash has positive impact on mechanical properties, it shortens the start of setting time of a mixture and it also increases early and later compressive strenghts.
|
|
|
Praparation and characterization of calcium aluminate hydrates
Hubáček, Václav ; Švec, Jiří (referee) ; Koplík, Jan (advisor)
This thesis deals with the preparation of pure calcium aluminate phases, specifically CA, CA2, C3A and C12A7 by two different methods - the solid state synthesis and the amorphous citrate method. The hydration of these phases at different temperatures was also studied The effect of the phase preparation method used and the simultaneous effect of temperature were observed on the prepared hydrates, using suitable analytical methods. The characterization and identification of the prepared phases and their hydrates were studied by X-ray diffraction analysis, Fourier transform infrared spectroscopy, scanning electron microscopy and simultaneous thermogravimetric and differential thermal analysis. The prepared hydration products were mostly identified in accordance with the literature data. TGA/DTA of the prepared hydrates helped to clarify some of the hydrate decomposition processes, especially for the hexagonal hydrate CAH10 and the cubic hydrate C3AH6, which were prepared in a sufficiently pure form suitable for analysis.
|
|
|
Hybride binders based on the high-calcium ash
Hubáček, Václav ; Cába, Vladislav (referee) ; Koplík, Jan (advisor)
The goal of this bachelor´s thesis was to develop a hybrid binder based on high calcium fly ash with the focus on addition of Portland cement, observation of hydration process, measurement of mechanichal properties, identification of hydration products and comparation with Portland cement. Hybrid binder was developer by adding different amounts of Portland cement to the selected mixture of high calcium fly ash activated by sodium hydroxide. Setting times and flexural strength and compressive strength were measured for these hybrid binders. Afterwards one type of hybrid binder was selected for more analyses (XFR, XRD, SEM/EDS and isothermic calorimetry). These analyses were also used for a sample of Portland cement and alkali activated high calcium fly ash and afterwards these three samples were compared between each other. The collected data show that the compositions of the activated fly ash and hybrid binder are very similar and the addition of Portland cement to the mixture has only a minor impact. Main hydration product for both of them was ettringite. Addition of Portland cement to the activated high calcium fly ash has positive impact on mechanical properties, it shortens the start of setting time of a mixture and it also increases early and later compressive strenghts.
|
guest ::
RSS feed.